| Naslov: | Production and characterization of lightweight aggregates from municipal solid waste incineration fly-ash through single- and double-step pelletization process |
|---|
| Avtorji: | ID Ferraro, Alberto (Avtor)
ID Ducman, Vilma (Avtor)
ID Colangelo, Francesco (Avtor)
ID Korat, Lidija (Avtor)
ID Spasiano, Danilo (Avtor)
ID Farina, Ilenia (Avtor) |
|---|
| Datoteke: |  URL - Izvorni URL, za dostop obiščite https://www.sciencedirect.com/science/article/pii/S0959652622048491?via%3Dihub
 PDF - Predstavitvena datoteka, prenos (8,90 MB)
MD5: 24CD86C2441569F809FD66D9907AEC74
PDF - Priloga, prenos (972,11 KB)
MD5: 2F60FC7002DB6F9098EAAB859040F1B0
To gradivo ima še več datotek. Celoten seznam je na voljo
spodaj. |
|---|
| Jezik: | Angleški jezik |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: |  ZAG - Zavod za gradbeništvo Slovenije
|
|---|
| Povzetek: | The performance of a cold-bonding pelletization process was investigated for lightweight aggregates (LWAs) production from municipal solid waste incineration (MSWI) fly-ash (FA), by including multiple waste materials in the aggregate mixture. Before pelletization, FA was pre-treated by washing with water, which led to a reduction of chloride (66.79%) and sulphate (25.30%) content. This was further confirmed by XRF and XRD analyses, which showed a reduction of chloride elements and the content of chlorine crystalline phases. The pelletization process was carried out using both single- and double-step methods. For single-step pelletization, all the mixtures contained 80% FA, combined with various compositions of cement (5, 10, and 15%) and granulated blast furnace slag (GBFS) (5, 10, and 15%). For the double-step pelletization 30% of cement and 70% of marble sludge (MS) were added to each of the previous mixtures. The apparent density of all the aggregates varied between 1.60 and 1.87 g cm 3, suggesting their suitability to be classified as LWAs. Aggregates produced from double-step pelletization showed improved characteristics, with water absorption capacity and open porosity generally lower compared to the corresponding aggregates from the single-step pelletization. The best values of compressive (crushing) strength (almost 11 MPa) were observed for double-step pelletization aggregates with initial cement: GBFS mixture of 15%:5%. Results from leaching tests showed an overall significant release of chloride and sulphate. Nevertheless, leaching from double-step pelletization aggregates was reduced by 1.73- 4.02 times for chloride and 1.58-5.67 times for sulphate, further suggesting that better performances are achievable through the addition of an aggregate second layer. |
|---|
| Ključne besede: | MSWI fly ash, lightweight aggregate, microtomography, open access |
|---|
| Status publikacije: | Objavljeno |
|---|
| Verzija publikacije: | Objavljena publikacija |
|---|
| Datum objave: | 26.11.2022 |
|---|
| Založnik: | Elsevier |
|---|
| Leto izida: | 2023 |
|---|
| Št. strani: | str. 1-11 |
|---|
| Številčenje: | Vol. 383 |
|---|
| PID: | 20.500.12556/DiRROS-16137  |
|---|
| UDK: | 620.1/.2 |
|---|
| ISSN pri članku: | 1879-1786 |
|---|
| DOI: | 10.1016/j.jclepro.2022.135275 |
|---|
| COBISS.SI-ID: | 133711363 |
|---|
| Avtorske pravice: | © 2022 The Authors. Published by Elsevier Ltd. |
|---|
| Opomba: | Nasl. z nasl. zaslona;
Opis vira z dne 13. 12. 2022;
Št. članka: 135275;
|
|---|
| Datum objave v DiRROS: | 03.05.2023 |
|---|
| Število ogledov: | 344 |
|---|
| Število prenosov: | 296 |
|---|
| Metapodatki: |     |
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |