| Naslov: | Complementary corrosion protection of cast AlSi7Mg0.3 alloy using Zr-Cr conversion and polyacrylic/siloxane-silica multilayer coatings |
|---|
| Avtorji: | ID Rodič, Peter, Institut "Jožef Stefan" (Avtor)
ID Kapun, Barbara, Institut "Jožef Stefan" (Avtor)
ID Milošev, Ingrid, Institut "Jožef Stefan" (Avtor) |
|---|
| Datoteke: |  URL - Izvorni URL, za dostop obiščite https://www.nature.com/articles/s41529-024-00467-5
 PDF - Predstavitvena datoteka, prenos (8,28 MB)
MD5: 0BCF588C68798D2157938A955BFFBE43
|
|---|
| Jezik: | Angleški jezik |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: |  IJS - Institut Jožef Stefan
|
|---|
| Povzetek: | Aluminium cast alloy AlSi7Mg0.3 is a lightweight metal commonly used in automotive, aeronautical and mechanical applications. It has good corrosion resistance but, under harsh operative conditions, would benefit from additional protection. In this study, a corrosion-protective multilayer coating system for AlSi7Mg0.3 based on hexafluoro-zirconated trivalent chromium coating (Zr-CrCC) and polyacrylic/siloxane-silica (PEHA-SS) coating was developed. The Zr-CrCC was formed by immersion of the substrate in a commercial conversion bath (SurTec® 650). PEHA-SS synthesis was based on organic precursors (2-ethylhexyl acrylate and [3-(methacryloyloxy)propyl]trimethoxysilane) and an inorganic precursor, tetraethyl orthosilicate. After deposition on AlSi7Mg0.3, each coating was first characterised individually, followed by the analysis of the multilayer using scanning electron microscopy and energy-dispersive X-ray spectroscopy. The adhesion of the coatings was evaluated with a cross-hatch cut test. The corrosion studies in sodium chloride solution using electrochemical impedance spectroscopy and salt spray testing showed that the multilayer system is superior to individual Zr-CrCC and PEHA-SS coatings. After 4 months in 0.1 M NaCl, the multilayer-coated samples exhibited the impedance at 10 mHz in the range of GΩ cm2, while scribed samples withstood the corrosion attack in a salt spray chamber for one week. Thus, albeit only about 100 nm thick, the Zr-CrCC deposited between the substrate and a 9-micrometre thick barrier sol-gel PEHA-SS coating acts as an active corrosion protection interlayer and contributes to the overall protectiveness of the multilayer system. |
|---|
| Ključne besede: | corrosion-protective, aluminium, material |
|---|
| Status publikacije: | Objavljeno |
|---|
| Verzija publikacije: | Objavljena publikacija |
|---|
| Poslano v recenzijo: | 21.10.2023 |
|---|
| Datum sprejetja članka: | 19.04.2024 |
|---|
| Datum objave: | 28.05.2024 |
|---|
| Založnik: | Springer Nature |
|---|
| Leto izida: | 2024 |
|---|
| Št. strani: | str. 1-16 |
|---|
| Številčenje: | Vol. 8, article no. 58 |
|---|
| Izvor: | Švica |
|---|
| PID: | 20.500.12556/DiRROS-22057  |
|---|
| UDK: | 620.1/.2 |
|---|
| ISSN pri članku: | 2397-2106 |
|---|
| DOI: | 10.1038/s41529-024-00467-5 |
|---|
| COBISS.SI-ID: | 197709827 |
|---|
| Avtorske pravice: | © The Author(s) 2024 |
|---|
| Opomba: | Nasl. z nasl. zaslona;
Opis vira z dne 4. 6. 2024;
|
|---|
| Datum objave v DiRROS: | 17.04.2025 |
|---|
| Število ogledov: | 573 |
|---|
| Število prenosov: | 263 |
|---|
| Metapodatki: |    |
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |