| Naslov: | Investigating the synergistic impact of freeze-thaw cycles and deicing salts on the properties of cementitious composites incorporating natural fibers and fly ash |
|---|
| Avtorji: | ID Merta, Ildikó (Avtor)
ID Zalar Serjun, Vesna (Avtor)
ID Mauko Pranjić, Alenka (Avtor)
ID Šajna, Aljoša (Avtor)
ID Štefančič, Mateja (Avtor)
ID Poletanovic, Bojan (Avtor)
ID Ameri, Farshad (Avtor)
ID Mladenović, Ana (Avtor) |
|---|
| Datoteke: |  URL - Izvorni URL, za dostop obiščite https://www.sciencedirect.com/science/article/pii/S2666790824001332
 PDF - Predstavitvena datoteka, prenos (10,99 MB)
MD5: E351A449375BCF87807D43F314A203D8
|
|---|
| Jezik: | Angleški jezik |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: |  ZAG - Zavod za gradbeništvo Slovenije
|
|---|
| Povzetek: | In cold climates, concrete structures confront durability challenges due to harsh conditions. This study evaluates the effects of incorporating natural fibers, such as hemp and flax fibers (at 1 vol%), and partially replacing cement with fly ash (at 25 and 50 wt%) on the properties of cementitious composites subjected to accelerated aging under freeze-thaw cycles and deicing salts. Findings reveal that natural fibers enhance the freeze-thaw resistance, reducing deterioration (scaling) to 5-8% after 56 cycles. When mortars were subjected to accelerated freeze-thaw cycles, the compressive strength of plain mortar significantly decreased (up to 57%). However, adding natural fibers to the matrix substantially reduced its compressive strength loss. In the case of flexural strength, plain mortars experienced 33% loss, while hemp, flax, and polypropylene fiber mortars showed only 13%, 23%, and 10% losses, respectively. Furthermore, mortars experience a notable enhancement in their energy absorption capacity when reinforced with natural fibers, particularly with hemp fibers (up to 348% higher than plain mortar). Under harsh conditions, hemp and flax-reinforced mortars, with 25wt% fly ash replacement, lose the compressive strength significantly however still demonstrate an alternative to synthetic fibers in terms of flexural strength. Even with 25wt% of fly ash, mortars with natural fiber reinforcement display significantly superior energy absorption capacities compared to plain mortars (up to 48%). |
|---|
| Ključne besede: | cementitious composites, natural fibers, freeze-thaw cycles, mechanical properties, mass loss, fly ash |
|---|
| Status publikacije: | Objavljeno |
|---|
| Verzija publikacije: | Objavljena publikacija |
|---|
| Datum objave: | 06.12.2024 |
|---|
| Založnik: | Elsevier Ltd. |
|---|
| Leto izida: | 2025 |
|---|
| Št. strani: | 1-46 str. |
|---|
| Številčenje: | Vol. 24, [article no.] 100853 |
|---|
| PID: | 20.500.12556/DiRROS-21105  |
|---|
| UDK: | 54 |
|---|
| ISSN pri članku: | 2666-7908 |
|---|
| DOI: | 10.1016/j.clet.2024.100853 |
|---|
| COBISS.SI-ID: | 218668547 |
|---|
| Avtorske pravice: | © 2024 The Authors. |
|---|
| Opomba: |
|
|---|
| Datum objave v DiRROS: | 23.12.2024 |
|---|
| Število ogledov: | 10 |
|---|
| Število prenosov: | 6 |
|---|
| Metapodatki: |    |
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |