| Naslov: | Enhancing ductility of hot-work tool steel through isothermal bainitic transformation |
|---|
| Avtorji: | ID Bajželj, Anže (Avtor)
ID Nagode, Aleš (Avtor)
ID Balaško, Tilen (Avtor)
ID Šetina, Barbara (Avtor)
ID Burja, Jaka (Avtor) |
|---|
| Datoteke: |  PDF - Predstavitvena datoteka, prenos (1,02 MB)
MD5: EADAA8E495A06DD36A759D32897534A5
 URL - Izvorni URL, za dostop obiščite https://www.confer.cz/metal/2023/4703-enhancing-ductility-of-hot-work-tool-steel-through-isothermal-bainitic-transformation
|
|---|
| Jezik: | Angleški jezik |
|---|
| Tipologija: | 1.08 - Objavljeni znanstveni prispevek na konferenci |
|---|
| Organizacija: |  IMT - Inštitut za kovinske materiale in tehnologije
|
|---|
| Povzetek: | Hot-work tool steels are extensively used in industrial applications that require high resistance to mechanical and chemical degradation at elevated temperatures. To meet these requirements, hot-work tool steels must exhibit good mechanical properties, including high tensile strength, hardness, wear resistance, and tempering resistance, as well as high thermal conductivity and ductility. This study investigates the ductility of the hot-work tool steel HTCS-130, which suffers from low ductility due to the presence of stable molybdenum-tungsten carbides (M6C) on the prior austenite crystal grain boundaries. Increasing austenitisation temperatures or prolonging the dwelling time at temperature can promote intensive migration of grain boundaries, leading to negative effects on the mechanical properties of the steel. To address this issue, isothermal transformation in the bainitic area between 350 and 500 °C was performed. Isothermal transformation at around 350 °C leads to the formation of lower bainite, which has similar hardness to tempered martensite. As the temperature of isothermal transformation increases, the hardness of the material decreases, due to the formation of upper bainite. The hardness analysis was measured using the Vickers method, the impact toughness of the steel samples was measured using a Charpy test with V-notched samples. The microstructure characterization was performed using optical and scanning electron microscopy. The improvement of ductility can be achieved by controlling the isothermal transformation of bainite and adjusting the heat treatment conHot-work tool steels are extensively used in industrial applications that require high resistance to mechanical and chemical degradation at elevated temperatures. To meet these requirements, hot-work tool steels must exhibit good mechanical properties, including high tensile strength, hardness, wear resistance, and tempering resistance, as well as high thermal conductivity and ductility. This study investigates the ductility of the hot-work tool steel HTCS-130, which suffers from low ductility due to the presence of stable molybdenum-tungsten carbides (M6C) on the prior austenite crystal grain boundaries. Increasing austenitisation temperatures or prolonging the dwelling time at temperature can promote intensive migration of grain boundaries, leading to negative effects on the mechanical properties of the steel. To address this issue, isothermal transformation in the bainitic area between 350 and 500 °C was performed. Isothermal transformation at around 350 °C leads to the formation of lower bainite, which has similar hardness to tempered martensite. As the temperature of isothermal transformation increases, the hardness of the material decreases, due to the formation of upper bainite. The hardness analysis was measured using the Vickers method, the impact toughness of the steel samples was measured using a Charpy test with V-notched samples. The microstructure characterization was performed using optical and scanning electron microscopy. The improvement of ductility can be achieved by controlling the isothermal transformation of bainite and adjusting the heat treatment conditions. These findings provide useful insights into the design and optimization of heat treatment processes for hot-work tool steels.ditions. These findings provide useful insights into the design and optimization of heat treatment processes for hot-work tool steels. |
|---|
| Ključne besede: | hot-work tool steel, austempering, bainitic transformation, ductility, dilatometry |
|---|
| Status publikacije: | Objavljeno |
|---|
| Verzija publikacije: | Objavljena publikacija |
|---|
| Založnik: | TANGER |
|---|
| Leto izida: | 2024 |
|---|
| Št. strani: | Str. 308-314 |
|---|
| Izvor: | Češka |
|---|
| PID: | 20.500.12556/DiRROS-18286  |
|---|
| UDK: | 669.14 |
|---|
| ISSN pri članku: | 2694-9296 |
|---|
| DOI: | 10.37904/metal.2023.4703 |
|---|
| COBISS.SI-ID: | 185399299 |
|---|
| Avtorske pravice: | Licenca Creative Commons je navedena na pristajalni strani članka (glej izvorni URL): "© This is an open access article distributed under the Creative Commons Attribution License (https://creativecommons.org/licenses/by/4.0/)". (Datum opombe 4. 4. 2023) |
|---|
| Opomba: | Nasl. z nasl. zaslona;
Opis vira z dne 14. 2. 2024;
|
|---|
| Datum objave v DiRROS: | 28.02.2024 |
|---|
| Število ogledov: | 679 |
|---|
| Število prenosov: | 248 |
|---|
| Metapodatki: |    |
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |