Povzetek: Alkali-activated materials (AAMs) represent a promising alternative to conventional building materials and ceramics. Being produced in large amounts as aluminosilicate-rich secondary products, such as slags, they can be utilized for the formulation of AAMs. Slags are partially crystalline metallurgical residues produced during the high temperature separation of metallic and non-metallic materials in the steelmaking processes. In the present study, the electric arc furnace carbon or stainless steel slag (EAF) and secondary metallurgical slag such as ladle furnace basic slag (LS) were used as precursors in an alkali-activation process. EAF slag, with its amorphous fraction of about 56%, presented higher contents of soluble Si and Al species with respect to ladle slag R (35%). However, both are suitable to produce AAM. The leaching behavior shows that all the release values are below the regulation limit. All the bivalent ions (Ba, Cd, Cu, Ni, Pb, and Zn) are well immobilized in a geopolymeric matrix, while amphoteric elements, such as As and Cr, show a slight increase of release with respect to the corresponding slag in alkaline and aqueous environments. In particular, for Sb and As of AAM, release still remains below the regulation limits, while Mo presents an increase of leaching values that slightly exceeds the limit for landfill non-dangerous waste.
Ključne besede: slag, aluminosilicate materials, chemical reactivity, cold consolidation, alkali activation, leaching test, open access
Objavljeno v DiRROS: 22.05.2023; Ogledov: 342; Prenosov: 174
Celotno besedilo (4,49 MB)
Gradivo ima več datotek! Več...

Povzetek: The results of phase 1 of an interlaboratory test, coordinated by the RILEM TC 267-TRM “Tests for Reactivity of Supplementary Cementitious Materials” showed that the R3 (rapid, relevant, reliable) test method, by measurement of heat release or bound water, provided the most reliable and relevant determination of the chemical reactivity of supplementary cementitious materials (SCMs), compared to other test methods. The phase 2 work, described in this paper aimed to improve the robustness of the test procedure and to develop precision statements for the consolidated test procedure. The effect of the pre-mixing and mixing conditions, and the impact of the mix design on the test method robustness were assessed and fixed for optimal conditions to carry out the R3 heat release test. The effect of the drying step was evaluated to define the R3 bound water test procedure in more detail. Finally, the robustness of the consolidated final test methods was determined by an interlaboratory study to define the precision statements.
Ključne besede: supplementary cementitious materials, reactivity test, bound water
Objavljeno v DiRROS: 26.04.2023; Ogledov: 315; Prenosov: 124
Celotno besedilo (1,07 MB)
Gradivo ima več datotek! Več...