Povzetek: Alkali activated foams have been extensively studied in recent years, due to their high performance and low environmental footprint compared to foams produced via other methods. Three types of fly ash differing in chemical and mineralogical composition and specific surface were used to synthesize alkali activated foams. Sodium perborate monohydrate was added as a foaming agent and sodium dodecyl sulphate as a stabilizing agent. Foams were characterized at room temperature and after exposure to an elevated temperature (1,000 °C). Densities from 1.2 down to 0.3 g/cm 3 were obtained, depending on the type of fly ash and quantity of foaming agent added. Correspondingly, compressive strength ranged from 1 to 6 MPa. Comparing all three fly ashes the most favorable results, in terms of density and corresponding compressive strength, were achieved from the fly ash with the highest amounts of SiO 2 and Al2 O 3 , as well as the highest amorphous phase content i.e., RI fly ash. Furthermore, after firing to 1,000 °C, the density of samples prepared using fly ash RI remained approximately the same, while the compressive strength increased on average by 50%. In the other two types of fly ash the density increased slightly after firing, due to significant shrinkage, and compressive strength increased by as much as 800%. X-ray powder diffraction analysis confirmed the occurrence of a crystallization process after firing to 1,000 ° C, which resulted in newly formed crystal phases, including nepheline, sodalite, tridymite, and gehlenite.
Ključne besede: foamed alkali activated materials, geopolymers, properties, micro-CT
Objavljeno v DiRROS: 22.08.2023; Ogledov: 256; Prenosov: 169
Celotno besedilo (7,94 MB)
Gradivo ima več datotek! Več...

Povzetek: Influence of particle size on the mechanical strength of alkali activated material from waste refractory monolithic was investigated in this study. Precursor was chemically and mineralogically analysed, separated on 4 fractions and alkali activated with Na-water glass. Alkali activated materials were thoroughly investigated under SEM and XRD to evaluate the not predicted differences in mechanical strength. Influence of curing temperature and time dependence at curing temperatures on mechanical strength were investigated in the sample prepared from a fraction that caused the highest compressive strength.
Ključne besede: refractory materials, alkali activation, particle size, SEM, XRF, XRD, compressive strength
Objavljeno v DiRROS: 21.08.2023; Ogledov: 354; Prenosov: 248
Celotno besedilo (13,36 MB)
Gradivo ima več datotek! Več...

Povzetek: Many standardised durability testing methods have been developed for Portland cement-based concretes, but require validation to determine whether they are also applicable to alkali-activated materials. To address this question, RILEM TC 247-DTA "Durability Testing of Alkali-Activated Materials" carried out round robin testing of carbonation and chloride penetration test methods, applied to five different alkali-activated concretes based on fly ash, blast furnace slag or metakaolin. The methods appeared overall to demonstrate an intrinsic precision comparable to their precision when applied to conventional concretes. The ranking of test outcomes for pairs of concretes of similar binder chemistry was satisfactory, but rankings were not always reliable when comparing alkali-activated concretes based on different precursors. Accelerated carbonation testing gave similar results for fly ash-based and blast furnace slag-based alkali-activated concretes, whereas natural carbonation testing did not. Carbonation of concrete specimens was observed to have occurred already during curing, which has implications for extrapolation of carbonation testing results to longer service life periods. Accelerated chloride penetration testing according to NT BUILD 443 ranked the tested concretes consistently, while this was not the case for the rapid chloride migration test. Both of these chloride penetration testing methods exhibited comparatively low precision when applied to blast furnace slag-based concretes which are more resistant to chloride ingress than the other materials tested.
Ključne besede: alkali-activated materials (AAM), carbonatization, chloride penetration, Rilem TC, durability
Objavljeno v DiRROS: 17.08.2023; Ogledov: 253; Prenosov: 170
Celotno besedilo (1014,30 KB)
Gradivo ima več datotek! Več...

Povzetek: The RILEM technical committee TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ conducted a round robin testing programme to determine the validity of various durability testing methods, originally developed for Portland cement based-concretes, for the assessment of the durability of alkali-activated concretes. The outcomes of the round robin tests evaluating sulfate resistance, alkali-silica reaction (ASR) and freeze–thaw resistance are presented in this contribution. Five different alkali-activated concretes, based on ground granulated blast furnace slag, fly ash, or metakaolin were investigated. The extent of sulfate damage to concretes based on slag or fly ash seems to be limited when exposed to an Na2SO4 solution. The mixture based on metakaolin showed an excessive, very early expansion, followed by a dimensionally stable period, which cannot be explained at present. In the slag-based concretes, MgSO4 caused more expansion and visual damage than Na2SO4; however, the expansion limits defined in the respective standards were not exceeded. Both the ASTM C1293 and RILEM AAR-3.1 test methods for the determination of ASR expansion appear to give essentially reliable identification of expansion caused by highly reactive aggregates. Alkali-activated materials in combination with an unreactive or potentially expansive aggregate were in no case seen to cause larger expansions; only the aggregates of known very high reactivity were seen to be problematic. The results of freeze–thaw testing (with/without deicing salts) of alkali-activated concretes suggest an important influence of the curing conditions and experimental conditions on the test outcomes, which need to be understood before the tests can be reliably applied and interpreted.
Ključne besede: alkali-activated materials/geopolymers, sulphate resistance, alkali silica reactivity, freeze-thaw resistance, Rilem TC
Objavljeno v DiRROS: 17.08.2023; Ogledov: 225; Prenosov: 163
Celotno besedilo (560,56 KB)
Gradivo ima več datotek! Več...

Povzetek: Alkali-activated foams (AAFs) present one of the most promising materials for use in the construction sector. Their main advantages lie in their utilization of waste material and their ability to form at temperatures well below 100 °C, while still competing in performance with foamed glass or ceramics. The present body of research has focused on improving the thermal stability of fly-ash foams by i) adding metakaolin, and ii) changing the activator from sodium-based to potassium-based components. It has been confirmed that a certain increase in thermal resistance is achieved through the addition of metakaolin while changing activators played a crucial role. While sodium-based AAFs without metakaolin start to shrink at approximately 600 °C, samples that have had metakaolin added start to shrink at approximately 700 °C. Samples without metakaolin that have used a potassium activator start to shrink at approximately 800 °C, whereas potassium-based samples with the addition of metakaolin start to shrink at approximately 900 °C.
Ključne besede: alkali activated materials, geopolymers, high temperature, resistance, foams
Objavljeno v DiRROS: 01.08.2023; Ogledov: 252; Prenosov: 198
Celotno besedilo (13,91 MB)
Gradivo ima več datotek! Več...