1. Use of steel slag for the synthesis of belite-sulfoaluminate clinkerLea Žibret, Martina Cvetković, Maruša Mrak, Mojca Loncnar, Andrej Ipavec, Sabina Dolenec, 2020, objavljeni znanstveni prispevek na konferenci Povzetek: Belite-sulfoaluminate (BCSA) cements are low-carbon mineral binders, which require low energy consumption and allow the incorporation of various secondary raw materials in the clinker raw meal. In this study two types of unprocessed steel slags, coming from stainless steel production, were incorporated in the BCSA clinkers. The clinker phase composition, clinker reactivity, and the compressive strength of the cement were studied to evaluate the possible use of the slag in BCSA clinkers. The cement clinkers were synthesized by using natural raw materials, white titanogypsum, mill scale, as well as two different steel slags: (i) EAF S slag, which is a by-product of melting the recycled steel scrap in an electric arc furnace, and (ii) la dle slag as a by-product of the processes of secondary metallurgy, in various quantities. Raw mixtures with two different targeted phase compositions varying in belite, calcium sulfoaluminate and ferrite phases were sintered at 1250 °C. Clinker phases were determined by Rietveld quantitative phase analysis, while their distribution, morphology and incorporation of foreign ions in the phases were studied by SEM/EDS analysis. The clinker reactivity was determined by isothermal calorimetry. BCSA cements were prepared by adding titanogypsum. The compressive strength of the cement pastes was determined after 7 days of hydration. The presence of a predicted major clinker phases was confirmed by Rietveld analysis, however periclase was also detected. Microscopy revealed subhedral grains of belite and euhedral grains of calcium sulfoaluminate phases, while ferrite occurred as an interstitial phase. The results showed differences in the microstructure and reactivity of the clinker and cement, which can be attributed to varying amounts of ettringite due to different slag types Ključne besede: belite-sulfoaluminate cement, cement clinker, steel slags, clinker microstructure, cement reactivity Objavljeno v DiRROS: 19.01.2024; Ogledov: 478; Prenosov: 205
Celotno besedilo (18,89 MB) Gradivo ima več datotek! Več... |
2. Phase development and hydration kinetics of belite-calcium sulfoaluminate cements at different curing temperaturesMaruša Mrak, Nina Daneu, Sabina Dolenec, 2020, izvirni znanstveni članek Povzetek: The influence of different curing temperatures on the hydration of belite-calcium sulfoaluminate cement was investigated at 20, 40 and 60 °C. The hydration kinetics and the hydrated phase assemblages were studied by isothermal calorimetry, X-ray powder diffraction, differential thermal analysis and thermogravimetric analysis, as well as field emission scanning electron microscopy. The compressive strength development of the cement pastes was also determined. Results showed that, at early ages, hydration was faster and early compressive strength was higher at elevated temperatures than at ambient temperature. On the other hand, at late ages in cement pastes cured at 60 °C, the amount of ettringite decreased, leading to lower compressive strength, indicating that the degree of hydration was lower at higher temperatures. Moreover, at elevated temperatures prismatic ettringite crystals became smaller due to faster hydration. Other hydration products present were aluminium hydroxide, which is formed together with ettringite from the hydration of calcium sulfoaluminate and gypsum, and C–S–H which precipitates as a main hydration product of belite. Belite hydrated in a lesser amount, especially at 60 °C, when the lowest amount of C–S–H was observed. Ključne besede: hydration, cement, temperature, belite, calcium sulfoaluminate, open access, hidratacija, cement, temperatura, belit, kalcijev sulfoaluminat Objavljeno v DiRROS: 04.08.2023; Ogledov: 493; Prenosov: 359
Celotno besedilo (7,33 MB) Gradivo ima več datotek! Več... |
3. The influence of calcium sulfate content on the hydration of belite-calcium sulfoaluminate cements with different clinker phase compositionsMaruša Mrak, Frank Winnefeld, Barbara Lothenbach, Sabina Dolenec, 2021, izvirni znanstveni članek Povzetek: The influence of different amounts of gypsum on the hydration of a belite-rich and a yeʼelimite-rich belite-calcium sulfoaluminate clinker (BCSA) was investigated. The hydration kinetics, phase assemblages and compressive strength development of cements prepared using yeʼelimite/ calcium sulfate molar ratios of 1, 1.5 and 2 were studied. Besides ettringite and monosulfate, aluminium hydroxide, strätlingite, C-S-H, iron-containing siliceous hydrogarnet and hydrotalcite were present as hydration products. Increasing the amount of gypsum increased the ratio of ettringite to monosulfate formed in the cement paste, lowered the amount of pore solution, delayed the dissolution of belite and ferrite, decreased the formation of strätlingite and, in the case of the yeʼelimite-rich BCSA, led to an increase in compressive strength. Increased amounts of belite in the clinker led to the formation of higher quantities of C-S-H, at the expense of straätlingite and a lower compressive strength, as belite has a lower degree of reaction than yeʼelimite and due to the formation of more C-S-H and stratlingite compared to the more space-filling ettringite. The thermodynamic model established for BCSA cement hydration agrees well with the experimental data. Compressive strength directly correlated with bound water from thermogravimetric analyses and inversely correlated with the porosity calculated from thermodynamic modelling. Ključne besede: belite-calcium sulfoaluminate cement, gypsum, hydration, thermodynamic modelling Objavljeno v DiRROS: 28.07.2023; Ogledov: 458; Prenosov: 359
Celotno besedilo (1,74 MB) Gradivo ima več datotek! Več... |
4. Building of the Al-Containing secondary raw materials registry for the production of low CO2 mineral binders in South-Eastern European regionGorazd Žibret, Klemen Teran, Lea Žibret, Katarina Šter, Sabina Dolenec, 2021, izvirni znanstveni članek Povzetek: The bottleneck in the process for increasing production of low CO2 mineral binders, based on BCSA (belite sulfoaluminate) clinkers, is the availability of Al-rich raw materials. For that purpose, a new registry of Al-containing secondary mineral residues (industrial and mine waste) has been developed and is presented in this paper. The methodology of creating the registry consists of three main steps: Gathering ideas, consolidation of ideas, and implementation. In order to achieve this, the following methodology was adopted: Analysis of similar registries by potential end-users and seeking potential solutions and tools to be used, and conducting 3 rounds of stakeholder consultations via workshops in order to determine crucial parameters and features the registry needs to contain. The key discussion points were about which data the registry needs to contain, who shall be the potential users, and what are the stakeholderʼs expectations from the registryʼs portal. Potential individual registry variables were identified as being relevant/irrelevant or available/unavailable, and potential solutions for the registrys sustainability were explored. Each Al-rich waste/residue data entry is divided into 10 slots, describing legal status, location, quantities, chemical (REE included), mineralogical, physical and radiological properties, life-cycle assessment, additional data, and data relevancy. The registry will act as a matchmaking tool between producers/holders of Al-rich secondary raw materials and potential producers of cement clinkers. Ključne besede: cement, belite sulfoaluminate clinker, waste, by--product, deležniki Objavljeno v DiRROS: 10.06.2022; Ogledov: 759; Prenosov: 421
Celotno besedilo (2,23 MB) Gradivo ima več datotek! Več... |