1. Stress corrosion crack initiation testing with tapered specimens in high-temperature water - results of a collaborative research projectRik-Wouter Bosch, Stefan Ritter, Matthias Herbst, Renate Kilian, Grace Burke, Jonathan Duff, Fabio Scenini, Yuchen Gu, Alice Dinu, Ulla Ehrnsten, Aki Toivonen, Radek Novotny, Oliver Martin, Francisco Javier Perosanz, Andraž Legat, Bojan Zajec, 2020, izvirni znanstveni članek Povzetek: The applicability of an accelerated test technique using tapered tensile specimens for investigating the stress corrosion crack (SCC) initiation behaviour of structural materials in high-temperature water was assessed in the framework of a European collaborative research project (MICRIN – MItigation of CRack INitiation). The main advantage of using a tapered geometry is, that in a single test a stress gradient is obtained through the gauge length, and therefore a stress threshold for SCC initiation can be determined in a reasonable timeframe. This method was used to investigate two different materials that were known to be susceptible to SCC in light water reactor environment: a high-Si stainless steel and a Ni-base weld metal (Alloy 182). The results of the international test programme confirmed that the tapered specimen test methodology could be used to identify a SCC initiation stress threshold, albeit that significant scatter was present in the data. Ključne besede: stress corrosion cracking, surface finish impact, tapered tensile specimen, autoclave, accelerated testing, light water nuclear reactor, critical threshold stress Objavljeno v DiRROS: 28.08.2023; Ogledov: 462; Prenosov: 253
Celotno besedilo (3,05 MB) Gradivo ima več datotek! Več... |
2. Effect of surface machining on the environmentally-assisted cracking of Alloy 182 and 316L stainless steel in light water reactor environments : results of the collaborative project MEACTOSMariia Zimina, Stefan Ritter, Bojan Zajec, Marc Vankeerberghen, Liberato Volpe, Anna Hojna, Rik-Wouter Bosch, Fabio Scenini, Zaiqing Que, Alberto Sáez-Maderuelo, P. Jill Meadows, Michael Grimm, Matthias Herbst, Andraž Legat, Agostino Maurotto, Radek Novotny, Karl-Heinz Seifert, 2023, izvirni znanstveni članek Povzetek: The main objective of the EU-funded project mitigating environmentally-assisted cracking through optimisation of surface condition (MEACTOS) was to gain knowledge on the ability of different surface machining procedures to mitigate environmentally-assisted cracking (EAC) in typical light water reactor structural materials and environments. Surfaces of cold-worked (CW) type 316L austenitic stainless steel and nickel-based weld metal Alloy 182 flat tapered tensile specimens were machined using different processes. EAC initiation susceptibility of these specimens was evaluated using constant extension rate tensile (CERT) tests under simulated boiling water reactor (BWR) and pressurized water reactor (PWR) conditions and assessed using constant load experiments. More than a hundred tests were performed covering about 10 years of autoclave testing time. Only minor or no measurable improvements in EAC initiation susceptibility as a function of surface treatments (grinding or advanced machining) compared to the standard industrial face milling were demonstrated. In most cases, the stress thresholds for EAC initiation determined in constant load tests confirmed the trend obtained from CERT tests. This paper summarises the most important results and conclusions concerning the EAC initiation behaviour for the CW 316L and Alloy 182 under reducing PWR and oxidizing BWR conditions. Ključne besede: crack initiation, environmentally-assisted cracking, Alloy 182, AISI 304 stainless steel, surface treatment, light water reactor, open access Objavljeno v DiRROS: 30.05.2023; Ogledov: 513; Prenosov: 283
Celotno besedilo (16,31 MB) Gradivo ima več datotek! Več... |