Povzetek: The crystallization of glass microspheres in the Y2O3–Al2O3-system produced from precursor powders of four different nominal compositions via flame synthesis is analyzed in detail by electron microscopy with a focus on electron backscatter diffraction (EBSD). Growth models are formulated for individual microspheres crystallized during flame synthesis as well as after an additional heat treatment step. 16 different types of crystallized bodies are cataloged for future reference. They are presented without regard for their relative occurrence; some are extremely rare but illustrate the possibilities of flame synthesis in the analyzed system. All three phases in the binary Y2O3–Al2O3-phase diagram (Y3Al5O12, YAlO3 and Y4Al2O9) and α-alumina are located by EBSD. Energy dispersive X-ray spectrometry results obtained from these microspheres show that their chemical composition can deviate from the nominal composition of the precursor powder. The multitude of differing microsphere types showing polygon and dendritic crystal growth as well as phase separation indicate that flame synthesis can lead to a wide variety of parameters during microsphere production, e.g. via irregular flight paths through the flame, contaminants or irregular cooling rates.
Ključne besede: Y2O3-Al2O3, microsphere crystallization, flame synthesis, EBSD
Objavljeno v DiRROS: 23.07.2024; Ogledov: 107; Prenosov: 91
Celotno besedilo (6,57 MB)
Gradivo ima več datotek! Več...

Povzetek: This study presents a comprehensive investigation of the formation, composition and behaviour of oxide layers during the high-temperature oxidation of four different steel alloys (16Mo3, 13Cr, T24 and P91) at a uniform temperature of 650 °C. The study is aimed at assessing the oxidation damage due to short-term overheating. The research combines CALPHAD (CALculation of PHAse Diagrams) calculations, thermogravimetric analysis (TGA) and advanced microscopy techniques, in- cluding scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD), to elucidate the complex mechanisms controlling oxidation kinetics and oxide layer development. CALPHAD calculations were used to determine the thermodynamically stable phases for each steel type at 650 ◦C and different oxygen activities. The results showed different phase compositions, highlighting the importance of the chromium content in steel for the formation of oxide layers. The different oxidation kinetics and oxide layer compositions are presented and associated with the increased risk of material degradation due to overheating. These results have significant implications for industrial applications, mainly the susceptibility to oxidation of low-alloyed steels like 16Mo3 and 13 Cr and contribute to a deeper understanding of oxidation processes in steels.
Ključne besede: high-temperature oxidation, thermogravimetric analysis, kinetics, CALPHAD, boiler steels, SEM, EBSD
Objavljeno v DiRROS: 26.01.2024; Ogledov: 439; Prenosov: 199
Celotno besedilo (12,99 MB)
Gradivo ima več datotek! Več...