1. Microstructural, corrosion and mechanical properties of a WE43 alloy : conventional extrusion versus SPDAnna Dobkowska, Aleksandra Zielińska, Irena Paulin, Črtomir Donik, Milena Koralnik, Bogusława Adamczyk-Cieślak, Monika Wieczorek-Czarnocka, Dariusz Kuc, Jiří Kubásek, Tomasz Mikuszewski, Matjaž Godec, Jarosław Mizera, 2024, izvirni znanstveni članek Povzetek: A hexagonal close-packed-structure WE43 alloy was extruded without any preheating of the initial billet using extrusion with an oscillating die to improve the corrosion and mechanical properties. The WE43 alloy was extruded at high ratios of R 1 5:1, R 2 7:1 and R 3 10:1. Electron back-scatter diffraction and transmission electron microscopy were used to determine the microstructural properties of the alloys. The influence of the extrusion method and the extrusion ratios on the corrosion and mechanical properties were investigated. Electrochemical tests were performed, and the corrosion damage was inspected. Tensile tests were made using micro specimens. When compared to conventional extrusion, the microstructural changes obtained with the KoBo method at R 5:1 increased the corrosion resistance, which was not only due to the grain refinement, but also due to the intensity of the texture. A decline in the corrosion resistance of the alloys deformed at higher extrusion ratios was observed. This was a result of the massive plastic strain imposed by the KoBo die. The room-temperature mechanical properties of the KoBo-extruded alloys were improved. However, at higher temperatures the mechanical properties decreased due to the solutioning of tiny triple precipitates. Ključne besede: WE43, several plastic deformation, microstructure, corrosion, mechanical properties Objavljeno v DiRROS: 23.07.2024; Ogledov: 112; Prenosov: 37
Povezava na datoteko |