| Naslov: | Deuterium retention and transport in ion-irradiated tungsten exposed to deuterium atoms : role of grain boundaries |
|---|
| Avtorji: | ID Markelj, Sabina, Institut "Jožef Stefan" (Avtor)
ID Zavašnik, Janez, Institut "Jožef Stefan" (Avtor)
ID Šestan, Andreja, Institut "Jožef Stefan" (Avtor)
ID Schwarz-Selinger, Thomas (Avtor)
ID Kelemen, Mitja, Institut "Jožef Stefan" (Avtor)
ID Punzón Quijorna, Esther, Institut "Jožef Stefan" (Avtor)
ID Alberti, Gabriele (Avtor)
ID Passoni, Mateo (Avtor)
ID Dellasega, David (Avtor) |
|---|
| Datoteke: |  URL - Izvorni URL, za dostop obiščite https://www.sciencedirect.com/science/article/pii/S2352179124000115?via%3Dihub
 PDF - Predstavitvena datoteka, prenos (7,06 MB)
MD5: 654956E2B41367F22BF0628520BC015B
|
|---|
| Jezik: | Angleški jezik |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: |  IJS - Institut Jožef Stefan
|
|---|
| Povzetek: | The influence of grain boundaries on deuterium (D) retention and transport was investigated in nanocrystalline tungsten (W) by exposing the samples to sub eV D atoms. Thin tungsten films with nanometer-sized grains were produced by pulsed laser deposition on tungsten substrates. Their grain size was increased up to one micrometer by thermal annealing in vacuum up to 1223 K. Irradiation damage was created by 20 MeV W ions at 290 K. The transmission electron microscopy analysis showed one order of magnitude larger dislocation density in nanometer-grained samples compared with the larger-grained samples. The samples were after W irradiation exposed to 0.3 eV D atoms at 600 K. D retention and D depth profiles were measured by nuclear reaction analysis. In the as-deposited nanometer-grained samples, D populated the damaged region more than three times faster than in the samples with larger grains, indicating that grain-boundaries increase D transport through the material. The concentration of defects was assessed by the final D concentration in the samples. The sample with a smallest grain size showed slightly larger D concentration in the irradiated area, but the difference in the D concentration is not substantial between different-grained samples. A large D concentration in the non-irradiated nanometer-grained sample was measured which is an indication for a high defect density in the initial material. From our observations, it can be postulated that the nanocrystalline microstructure did not substantially influence the generation of irradiation-induced defects by defect annihilation at grain boundaries. |
|---|
| Ključne besede: | deuterium, tungsten, grain boundaries, transport, displacement damage, retention |
|---|
| Status publikacije: | Objavljeno |
|---|
| Verzija publikacije: | Objavljena publikacija |
|---|
| Poslano v recenzijo: | 15.11.2023 |
|---|
| Datum sprejetja članka: | 08.01.2024 |
|---|
| Datum objave: | 09.01.2024 |
|---|
| Založnik: | Elsevier |
|---|
| Leto izida: | 2024 |
|---|
| Št. strani: | str. 1-25 |
|---|
| Številčenje: | Vol. 38, Vol. , [article no.] 101589 |
|---|
| Izvor: | Nizozemska |
|---|
| PID: | 20.500.12556/DiRROS-24683  |
|---|
| UDK: | 53 |
|---|
| ISSN pri članku: | 2352-1791 |
|---|
| DOI: | 10.1016/j.nme.2024.101589 |
|---|
| COBISS.SI-ID: | 180564483 |
|---|
| Avtorske pravice: | © 2024 The Authors. |
|---|
| Opomba: | Nasl. z nasl. zaslona;
Soavtorji iz Slovenije: J. Zavašnik, A. Šestan, M. Kelemen, E. Punzón-Quijorna;
Opis vira z dne 11. 1. 2024;
|
|---|
| Datum objave v DiRROS: | 12.12.2025 |
|---|
| Število ogledov: | 57 |
|---|
| Število prenosov: | 34 |
|---|
| Metapodatki: |    |
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |