Abstract: The ever-growing worldwide demand for fired clay brick has resulted in the shortage of clay in many parts of the world. Therefore, there is a need to look for more sustainable alternative materials for the brick manufacturing. This study has investigated the potential use of the untreated Drava River sediment as a substitute material for clay in the production of fired bricks, with the research being conducted at both laboratory and industrial level. At the laboratory level, brick specimens were prepared by mixing clay with different river sediment proportions (ranging from 10 to 50 wt%) and were fired at 950 °C, with microstructural and various physical–mechanical properties being analyzed. Elevated carbonate content in Drava river sediment results in higher weight loss during firing at temperatures up to 950 °C, comparing to firing pure brick-making clay. Consequently, the addition of sediment increases porosity of fired bricks, which results in lowering of their mechanical properties. Results reveal that the compressive strength of the pure clay sample was 79.5 MPa, while the compressive strength of the sample with the addition of river sediment from 10 wt% to 50 wt% decreased from 73.9 MPa to 26.2 MPa, respectively. Despite the lower compressive strength, the 26.2 MPa is still above the limit value of 10 MPa specified in the standard EN 772–1 [1]. At the industrial level, hollow clay bricks were prepared with 20 wt% of the river sediment and fired in a tunnel kiln. Inclusion of the river sediment also decreased compressive strength from 38 MPa for pure mixture to 26 MPa for 20 wt% of the sediment addition, confirming usability of Drava sediment in brick production. In addition, LCA study has been conducted to evaluate the environmental impacts associated with the industrial production of classic bricks and bricks with the addition of the river sediment. The obtained results have shown that the bricks made with the addition of the Drava River sediment are sustainable and environmentally friendly and meet all the requirements specified in the relevant regulatory standard.
Keywords: sediments, clay masonry units, LCA, properties
Published in DiRROS: 30.05.2023; Views: 294; Downloads: 217
Full text (4,76 MB)
This document has many files! More...

Abstract: Materials for biomedical applications often need to be coated to enhance their performance, such as their biocompatibility, antibacterial, antioxidant, and anti-inflammatory properties, or to assist the regeneration process and influence cell adhesion. Among naturally available substances, chitosan meets the above criteria. Most synthetic polymer materials do not enable the immobilization of the chitosan film. Therefore, their surface should be altered to ensure the interaction between the surface functional groups and the amino or hydroxyl groups in the chitosan chain. Plasma treatment can provide an effective solution to this problem. This work aims to review plasma methods for surface modification of polymers for improved chitosan immobilization. The obtained surface finish is explained in view of the different mechanisms involved in treating polymers with reactive plasma species. The reviewed literature showed that researchers usually use two different approaches: direct immobilization of chitosan on the plasma-treated surface or indirect immobilization by additional chemistry and coupling agents, which are also reviewed. Although plasma treatment leads to remarkably improved surface wettability, this was not the case for chitosan-coated samples, where a wide range of wettability was reported ranging from almost superhydrophilic to hydrophobic, which may have a negative effect on the formation of chitosan-based hydrogels.
Keywords: polymer surfaces, chitosan, coatings, plasma-surface modification, adhesion
Published in DiRROS: 24.02.2023; Views: 405; Downloads: 218
Full text (6,88 MB)
This document has many files! More...

Keywords: onkologija, rak dojke, obsevanje
Published in DiRROS: 09.02.2023; Views: 329; Downloads: 103
Full text (40,23 KB)

Published in DiRROS: 13.01.2023; Views: 599; Downloads: 145
Full text (1,62 MB)

Abstract: A method for the immobilization of an antibacterial chitosan coating to polymeric urinary medical catheters is presented. The method comprises a two-step plasma-treatment procedure, followed by the deposition of chitosan from the water solution. In the first plasma step, the urinary catheter is treated with vacuum-ultraviolet radiation to break bonds in the polymer surface film and create dangling bonds, which are occupied by hydrogen atoms. In the second plasma step, polymeric catheters are treated with atomic oxygen to form oxygen-containing surface functional groups acting as binding sites for chitosan. The presence of oxygen functional groups also causes a transformation of the hydrophobic polymer surface to hydrophilic, thus enabling uniform wetting and improved adsorption of the chitosan coating. The wettability was measured by the sessile-drop method, while the surface composition and structure were measured by X-ray photoelectron spectroscopy and Fourier-transform infrared spectroscopy. Non-treated samples did not exhibit successful chitosan immobilization. The effect of plasma treatment on immobilization was explained by noncovalent interactions such as electrostatic interactions and hydrogen bonds.
Keywords: polymer, chitosan immobilization, adhesion, plasma-surface modification, biopolymers
Published in DiRROS: 05.12.2022; Views: 478; Downloads: 291
Full text (6,47 MB)
This document has many files! More...