Comparison of the mineralogy and microstructure of EAF stainless steel slags with reference to the cooling treatment
Mojca Loncnar, Ana Mladenovič, Marija Zupančič, Peter Bukovec, 2017, original scientific article

Abstract: TIn the present study the differences in the mineralogical composition and microstructure of various types of EAF stainless steel (EAF S) slag with regard to the cooling treatment, the operation practice in an EAF (electric arc furnace) and environmental ageing reactions were evaluated. It was shown that the mineralogy of the investigated EAF S slags varied from one slag to another, depending on the quality of the produced stainless steel. The production process of the treated steel also has a strong influence on the mineralogy of the slags. The conditions during water cooling treatment were not sufficient to prevent the crystallization of primary mineral phases, which occurs predominantly in air-cooled EAF S slags, probably due to the high basicity of the investigated slags. However, the water cooling treatment of hot slag leads to the absence of γ-CaSiO 4 and the formation of secondary mineral phases predominantly calcite, portlandite, ettringite, calcium aluminate hydrate and calcium silicate hydrate. It has been shown that during the environmental ageing test (down-flow column test) secondary mineral phases were formed, which were the same as those formed during the water cooling treatment.
Keywords: electric arc furnace stainless steel slag, cooling path, microstructure, mineralogy
Published in DiRROS: 14.08.2024; Views: 39; Downloads: 68
.pdf Full text (3,74 MB)
This document has many files! More...

2.
Particle size manipulation as an influential parameter in the development of mechanical properties in electric arc furnace slag-based AAM
Katja Traven, Mark Češnovar, Vilma Ducman, 2019, original scientific article

Abstract: Alkali-activated materials (AAM) have gained recognition as a promising alternative to technical ceramic and building materials owing to the lower energy demands for production and the potential to use slag as a precursor. In the present study, five sets of slag-based AAM pastes were prepared with different particle sizes (fractions d < 63, 63 < d < 90, and 90 < d < 125 μm in different mass ratios) under the same curing regime and using a fixed precursor to activator (water) mass ratio. Precursors and the hardened AAM are evaluated using BET, XRD, XRF, SEM, FTIR, reactivity of precursors by leaching, and mercury intrusion porosimetry (MIP). Chemical analysis indicated only marginal differences among the different-sized fractions of input materials, whereas the BET surface area and reactivity among the precursors differed significantly-smaller particles had the largest surface area, and thus, higher reactivity. The mineralogical differences between the precursors and hardened AAM were negligible. The results revealed that compressive strength was significantly influenced by particle size, i.e., a threefold increase in strength when the particle size was halved. Microstructural evaluation using MIP confirmed that the porosity was the lowest in AAM with the smallest particle size. The low porosity and high reactivity of the fine fractions led to the highest compressive strength, confirming that manipulation of particle size can significantly influence the mechanical properties.
Keywords: alkalijsko aktivirani materiali, žlindra iz obločne peči, mehanska aktivacija, mehanske lastnosti, poroznost, alkali-activated materials (AAM), electric arc furnace steel slag, mechanical activation, mechanical properties, porosity