1. Use of steel slag for the synthesis of belite-sulfoaluminate clinkerLea Žibret, Martina Cvetković, Maruša Mrak, Mojca Loncnar, Andrej Ipavec, Sabina Dolenec, 2020, published scientific conference contribution Abstract: Belite-sulfoaluminate (BCSA) cements are low-carbon mineral binders, which require low energy consumption and allow the incorporation of various secondary raw materials in the clinker raw meal. In this study two types of unprocessed steel slags, coming from stainless steel production, were incorporated in the BCSA clinkers. The clinker phase composition, clinker reactivity, and the compressive strength of the cement were studied to evaluate the possible use of the slag in BCSA clinkers. The cement clinkers were synthesized by using natural raw materials, white titanogypsum, mill scale, as well as two different steel slags: (i) EAF S slag, which is a by-product of melting the recycled steel scrap in an electric arc furnace, and (ii) la dle slag as a by-product of the processes of secondary metallurgy, in various quantities. Raw mixtures with two different targeted phase compositions varying in belite, calcium sulfoaluminate and ferrite phases were sintered at 1250 °C. Clinker phases were determined by Rietveld quantitative phase analysis, while their distribution, morphology and incorporation of foreign ions in the phases were studied by SEM/EDS analysis. The clinker reactivity was determined by isothermal calorimetry. BCSA cements were prepared by adding titanogypsum. The compressive strength of the cement pastes was determined after 7 days of hydration. The presence of a predicted major clinker phases was confirmed by Rietveld analysis, however periclase was also detected. Microscopy revealed subhedral grains of belite and euhedral grains of calcium sulfoaluminate phases, while ferrite occurred as an interstitial phase. The results showed differences in the microstructure and reactivity of the clinker and cement, which can be attributed to varying amounts of ettringite due to different slag types Keywords: belite-sulfoaluminate cement, cement clinker, steel slags, clinker microstructure, cement reactivity Published in DiRROS: 19.01.2024; Views: 470; Downloads: 197
Full text (18,89 MB) This document has many files! More... |
2. Experimental study and thermodynamic modelling of the temperature effect on the hydration of belite-ye’elimite-ferrite cementsMaruša Mrak, Frank Winnefeld, Barbara Lothenbach, Andraž Legat, Sabina Dolenec, 2024, original scientific article Abstract: This study focuses on the kinetics of hydration, phase assemblage, microstructure and mechanical properties after various hydration times of two different BCSA cements at 5, 20, 40 and 60 ◦C and compares experimental data with thermodynamic modelling. Different curing temperatures change the type of hydrates and their amounts. Ye’elimite and gypsum in belite-ye’elimite-ferrite cements are almost fully reacted after 24 h of hydration at 20, 40 and 60 ◦C, while not at 5 ◦C. The hydration of belite is slower than the one of ye’elimite, but reaches a high degree of hydration after 150 days which is increasing with temperature. Less ettringite is present at elevated temperatures due to its increasing solubility, while more monosulfate is observed. Furthermore, with increasing temperature siliceous hydrogarnet forms at the expenses of strätlingite as well as more C S H is found as more belite reacts resulting in higher compressive strength. Dense and homogenous microstructure is observed at 5 ◦C, while it is more heterogeneous at higher temperatures. The presence of more ye’elimite resulted in higher ettringite and str¨atlingite formation and a higher compressive strength, while more belite yields more C S H in the hydrates and lower compressive strength. Keywords: belite-ye’elimite-ferrite cement, temperature, hydration, thermodynamic modelling Published in DiRROS: 11.12.2023; Views: 359; Downloads: 272
Full text (9,96 MB) This document has many files! More... |
3. Phase development and hydration kinetics of belite-calcium sulfoaluminate cements at different curing temperaturesMaruša Mrak, Nina Daneu, Sabina Dolenec, 2020, original scientific article Abstract: The influence of different curing temperatures on the hydration of belite-calcium sulfoaluminate cement was investigated at 20, 40 and 60 °C. The hydration kinetics and the hydrated phase assemblages were studied by isothermal calorimetry, X-ray powder diffraction, differential thermal analysis and thermogravimetric analysis, as well as field emission scanning electron microscopy. The compressive strength development of the cement pastes was also determined. Results showed that, at early ages, hydration was faster and early compressive strength was higher at elevated temperatures than at ambient temperature. On the other hand, at late ages in cement pastes cured at 60 °C, the amount of ettringite decreased, leading to lower compressive strength, indicating that the degree of hydration was lower at higher temperatures. Moreover, at elevated temperatures prismatic ettringite crystals became smaller due to faster hydration. Other hydration products present were aluminium hydroxide, which is formed together with ettringite from the hydration of calcium sulfoaluminate and gypsum, and C–S–H which precipitates as a main hydration product of belite. Belite hydrated in a lesser amount, especially at 60 °C, when the lowest amount of C–S–H was observed. Keywords: hydration, cement, temperature, belite, calcium sulfoaluminate, open access, hidratacija, cement, temperatura, belit, kalcijev sulfoaluminat Published in DiRROS: 04.08.2023; Views: 486; Downloads: 355
Full text (7,33 MB) This document has many files! More... |
4. The influence of calcium sulfate content on the hydration of belite-calcium sulfoaluminate cements with different clinker phase compositionsMaruša Mrak, Frank Winnefeld, Barbara Lothenbach, Sabina Dolenec, 2021, original scientific article Abstract: The influence of different amounts of gypsum on the hydration of a belite-rich and a yeʼelimite-rich belite-calcium sulfoaluminate clinker (BCSA) was investigated. The hydration kinetics, phase assemblages and compressive strength development of cements prepared using yeʼelimite/ calcium sulfate molar ratios of 1, 1.5 and 2 were studied. Besides ettringite and monosulfate, aluminium hydroxide, strätlingite, C-S-H, iron-containing siliceous hydrogarnet and hydrotalcite were present as hydration products. Increasing the amount of gypsum increased the ratio of ettringite to monosulfate formed in the cement paste, lowered the amount of pore solution, delayed the dissolution of belite and ferrite, decreased the formation of strätlingite and, in the case of the yeʼelimite-rich BCSA, led to an increase in compressive strength. Increased amounts of belite in the clinker led to the formation of higher quantities of C-S-H, at the expense of straätlingite and a lower compressive strength, as belite has a lower degree of reaction than yeʼelimite and due to the formation of more C-S-H and stratlingite compared to the more space-filling ettringite. The thermodynamic model established for BCSA cement hydration agrees well with the experimental data. Compressive strength directly correlated with bound water from thermogravimetric analyses and inversely correlated with the porosity calculated from thermodynamic modelling. Keywords: belite-calcium sulfoaluminate cement, gypsum, hydration, thermodynamic modelling Published in DiRROS: 28.07.2023; Views: 457; Downloads: 348
Full text (1,74 MB) This document has many files! More... |
5. Building of the Al-Containing secondary raw materials registry for the production of low CO2 mineral binders in South-Eastern European regionGorazd Žibret, Klemen Teran, Lea Žibret, Katarina Šter, Sabina Dolenec, 2021, original scientific article Abstract: The bottleneck in the process for increasing production of low CO2 mineral binders, based on BCSA (belite sulfoaluminate) clinkers, is the availability of Al-rich raw materials. For that purpose, a new registry of Al-containing secondary mineral residues (industrial and mine waste) has been developed and is presented in this paper. The methodology of creating the registry consists of three main steps: Gathering ideas, consolidation of ideas, and implementation. In order to achieve this, the following methodology was adopted: Analysis of similar registries by potential end-users and seeking potential solutions and tools to be used, and conducting 3 rounds of stakeholder consultations via workshops in order to determine crucial parameters and features the registry needs to contain. The key discussion points were about which data the registry needs to contain, who shall be the potential users, and what are the stakeholderʼs expectations from the registryʼs portal. Potential individual registry variables were identified as being relevant/irrelevant or available/unavailable, and potential solutions for the registrys sustainability were explored. Each Al-rich waste/residue data entry is divided into 10 slots, describing legal status, location, quantities, chemical (REE included), mineralogical, physical and radiological properties, life-cycle assessment, additional data, and data relevancy. The registry will act as a matchmaking tool between producers/holders of Al-rich secondary raw materials and potential producers of cement clinkers. Keywords: cement, belite sulfoaluminate clinker, waste, by--product, deležniki Published in DiRROS: 10.06.2022; Views: 752; Downloads: 415
Full text (2,23 MB) This document has many files! More... |