1. Analysis of alkali-activated mineral wool-slag binders : evaluating the differences between one-part and two-part variationsElijah Adesanya, Rawia Dabbebi, Christine Rößler, Majda Pavlin, Zhenming Li, Tero Luukkonen, Juho Yliniemi, Mirja Illikainen, 2024, original scientific article Abstract: Two synthesis pathways (one- and two-part) in alkali-activated binders were compared using ground granulated blast furnace slag (GGBFS), mineral wool (MW) activated using dry and liquid alkali activators with similar Na2O/SiO2 modulus. The effect of activator type on reaction kinetics, strength development, setting times, and durability shows that one-part synthesis does not only improve early strength, but also provide better durability properties. While the highest compressive strength (56 MPa, 90 days) was achieved for the one-part mix (DM), the reaction products (presence of Mg–Al layered double hydroxide and C–S–H-like phases) observed for both mortar mixes were similar. The DM mortars showed better resistance to sulfate attack than two-part mix (WM) mortars and sets faster. The results highlight the significance of the one-part pathways in the synthesis of alkali-activated materials. Keywords: recycling, alkali activated material, mineral wool Published in DiRROS: 11.03.2024; Views: 323; Downloads: 256
Full text (1,28 MB) This document has many files! More... |
2. Antibacterial properties and cytotoxicity of 100% waste derived alkali activated materials : slags and stone wool-based bindersCaterina Sgarlata, Giovanni Dal Poggetto, Federica Piccolo, Michelina Catauro, Katja Traven, Mark Češnovar, Hoang Nguyen, Juho Yliniemi, Luisa Barbieri, Vilma Ducman, Isabella Lancellotti, Cristina Leonelli, 2021, original scientific article Abstract: In this study we compare the leaching behavior and the antibacterial and cytotoxic properties of 100% slag or stone wool derived alkali activated materials. The antibacterial activity was measured as the inhibiting capacity against two Gram- negative bacterial strains, Escherichia coli and Pseudomonas aeruginosa and one Gram-positive bacterial strain: Enterococcus faecalis. The cytotoxicity properties were tested on mouse embryonic fibroblast NIH-3T3 cell-line. It was proved that the high quality of the 3D aluminosilicate network of the consolidated materials obtained from powders of CaO or MgO-rich slags or stone wool, opportunely activated with NaO and/or Na-silicate, was capable of stabilizing heavy metal cations. The concentrations of leachate heavy cations were lower than the European law limit when tested in water. The effect of additives in the composites, basal fibers or nanocellulose, did not reduce the chemical stability and slightly influenced the compressive strength. Weight loss in water increased by 20% with basalt fibers addition, while it remained almost constant when nanocellulose was added. All the consolidated materials, cement-like in appearance, exhibited limited antibacterial properties (viability from 50 to 80% depending on the bacterial colony and the amount of sample) and absence of cytotoxicity, envisaging good acceptance from part of the final consumer and zero ecological impact. CaO-rich formulations can replace ordinary Portland cement (showing bacterial viability at 100%) with a certain capability for preventing the reproduction of the E. coli and S. aureus bacteria with health and environmental protection results. Keywords: antibacterial properties, cytotoxicity, alkali-activated materials, slag, stone wool, waste utilization, social acceptance Published in DiRROS: 22.05.2023; Views: 507; Downloads: 323
Full text (2,31 MB) This document has many files! More... |