| Naslov: | Influence of isothermal annealing in the 600 to 750 °C range on the degradation of SAF 2205 duplex stainless steel |
|---|
| Avtorji: | ID Burja, Jaka (Avtor)
ID Žužek, Borut (Avtor)
ID Šetina, Barbara (Avtor) |
|---|
| Datoteke: |  PDF - Predstavitvena datoteka, prenos (20,91 MB)
MD5: 9F6F55F5C1C3B33F0D073759EDF629FC
 URL - Izvorni URL, za dostop obiščite https://www.mdpi.com/2624-5558/5/3/14
|
|---|
| Jezik: | Angleški jezik |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: |  IMT - Inštitut za kovinske materiale in tehnologije
|
|---|
| Povzetek: | We studied the effect of isothermal annealing (600–750 °C, 1 to 1000 min) on the microstructure
and mechanical properties of SAF 2205 duplex stainless steel. Impact toughness was found
to be significantly more affected than hardness by annealing. Annealing at 750 °C for 1000 min
resulted in a more than 90% decrease in impact toughness, while hardness only increased by 25%.
Tensile strength increased up to 100 MPa, but elongation decreased by more than 50% under the
same conditions. Sigma phase formation was minimal at lower temperatures (650 °C and below)
but increased significantly at higher temperatures. At 750 °C and 1000 min of annealing, the ferrite
content dropped from 50% to 16%. These findings suggest that annealing temperature and time need
to be carefully controlled to avoid a reduction in impact toughness and ductility caused by sigma
phase precipitation. The harmful effect of sigma phase precipitation on mechanical properties was
directly shown.
|
|---|
| Ključne besede: | duplex stainless steel, sigma phase, precipitation kinetics, mechanical properties, isothermal annealing |
|---|
| Status publikacije: | Objavljeno |
|---|
| Verzija publikacije: | Objavljena publikacija |
|---|
| Datum objave: | 12.07.2024 |
|---|
| Založnik: | MDPI |
|---|
| Leto izida: | 2024 |
|---|
| Št. strani: | str. 340-349 |
|---|
| Številčenje: | Vol. 5, iss. 3 |
|---|
| Izvor: | Švica |
|---|
| PID: | 20.500.12556/DiRROS-19729  |
|---|
| UDK: | 669.14.018.8-153:620.1 |
|---|
| ISSN pri članku: | 2624-5558 |
|---|
| DOI: | 10.3390/cmd5030014 |
|---|
| COBISS.SI-ID: | 202622979 |
|---|
| Avtorske pravice: | © 2024 by the authors |
|---|
| Opomba: | Nasl. z nasl. zaslona;
Opis vira z dne 24. 7. 2024;
|
|---|
| Datum objave v DiRROS: | 24.07.2024 |
|---|
| Število ogledov: | 298 |
|---|
| Število prenosov: | 239 |
|---|
| Metapodatki: |    |
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |