| Naslov: | Development of multi-component fluoropolymer based coating on simulated outdoor patina on quaternary bronze |
|---|
| Avtorji: | ID Kosec, Tadeja (Avtor)
ID Škrlep, Luka (Avtor)
ID Švara Fabjan, Erika (Avtor)
ID Sever Škapin, Andrijana (Avtor)
ID Masi, Giulia (Avtor)
ID Bernardi, Elena (Avtor)
ID Chiavari, Cristina (Avtor)
ID Josse, Claudie (Avtor)
ID Esvan, Jerome (Avtor)
ID Robbiola, Luc (Avtor) |
|---|
| Datoteke: |  URL - Izvorni URL, za dostop obiščite https://www.sciencedirect.com/science/article/pii/S0300944018309743
 PDF - Predstavitvena datoteka, prenos (2,17 MB)
MD5: 44C73068975F40C4A2B187817E775FE8
 DOCX - Priloga, prenos (14,46 KB)
MD5: 1BE8DEF9048A441030F020B67649A39C
|
|---|
| Jezik: | Angleški jezik |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: |  ZAG - Zavod za gradbeništvo Slovenije
|
|---|
| Povzetek: | Bronze reacts with oxygen, humidity, and pollutants in the atmosphere so that a patina forms. Natural exposure to an outdoor atmosphere can be simulated and accelerated in order to achieve a patina that mimics outdoor ancient patina. In order to avoid the uncontrolled dissolving of either the natural or artificially formed patina, protection of the patina is needed.
In this study, a multi-component fluoropolymer based coating for the protection of bronze patina was developed. In order to provide various functionalities of the coating (such as the hydrophobicity of the coating surface, obtaining interactions within the coating itself as well as a bronze substrate and inhibiting the corrosion processes), a fluoroacrylate coating with appropriate adhesion promoter was suggested, with and without a silane modified benzotriazole inhibitor. The protective efficiency and durability of the applied coatings were investigated electrochemically using potentiodynamic tests and electrochemical impedance spectroscopy in a simulated acid rain solution. All of the developed coatings showed a significant decrease in the corrosion current density. The self-assembled single layer coating (FA-MS) also showed 100% inhibition efficiency. After ageing the coating remained transparent and did not change by UV exposure and/or thermal cycling. The patina and coating investigations using FIB-SEM and EDX showed that the latter coating (FA-MS) successfully covered the surface of the patinated bronze. The mechanism of the bonding was proposed and supported with the spectroscopic observation of a thin and even coating.
|
|---|
| Ključne besede: | bronze, patina, fluoropolymer coating, atmospheric corrosion |
|---|
| Status publikacije: | Objavljeno |
|---|
| Verzija publikacije: | Objavljena publikacija |
|---|
| Datum objave: | 23.02.2019 |
|---|
| Založnik: | Elsevier Sequoia |
|---|
| Leto izida: | 2019 |
|---|
| Št. strani: | str. 27-35 |
|---|
| Številčenje: | Vol. 131 |
|---|
| PID: | 20.500.12556/DiRROS-17186  |
|---|
| UDK: | 544.5/.6 |
|---|
| ISSN pri članku: | 0300-9440 |
|---|
| DOI: | 10.1016/j.porgcoat.2019.01.040 |
|---|
| COBISS.SI-ID: | 2430055 |
|---|
| Avtorske pravice: | © 2019 The Authors. Published by Elsevier B.V. |
|---|
| Datum objave v DiRROS: | 25.10.2023 |
|---|
| Število ogledov: | 775 |
|---|
| Število prenosov: | 451 |
|---|
| Metapodatki: |    |
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |