| Naslov: | Stress corrosion crack initiation testing with tapered specimens in high-temperature water - results of a collaborative research project |
|---|
| Avtorji: | ID Bosch, Rik-Wouter (Avtor)
ID Ritter, Stefan (Avtor)
ID Herbst, Matthias (Avtor)
ID Kilian, Renate (Avtor)
ID Burke, Grace (Avtor)
ID Duff, Jonathan (Avtor)
ID Scenini, Fabio (Avtor)
ID Gu, Yuchen (Avtor)
ID Dinu, Alice (Avtor)
ID Ehrnsten, Ulla (Avtor)
ID Toivonen, Aki (Avtor)
ID Novotny, Radek (Avtor)
ID Martin, Oliver (Avtor)
ID Perosanz, Francisco Javier (Avtor)
ID Legat, Andraž (Avtor)
ID Zajec, Bojan (Avtor) |
|---|
| Datoteke: |  URL - Izvorni URL, za dostop obiščite https://www.tandfonline.com/doi/full/10.1080/1478422X.2020.1815460?scroll=top&needAccess=true
Opis: Odprti dostop
 PDF - Predstavitvena datoteka, prenos (3,05 MB)
MD5: F2723E606FB815BFA1B5A2E9C9CCF539
|
|---|
| Jezik: | Angleški jezik |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: |  ZAG - Zavod za gradbeništvo Slovenije
|
|---|
| Povzetek: | The applicability of an accelerated test technique using tapered tensile specimens for investigating the stress corrosion crack (SCC) initiation behaviour of structural materials in high-temperature water was assessed in the framework of a European collaborative research project (MICRIN – MItigation of CRack INitiation). The main advantage of using a tapered geometry is, that in a single test a stress gradient is obtained through the gauge length, and therefore a stress threshold for SCC initiation can be determined in a reasonable timeframe. This method was used to investigate two different materials that were known to be susceptible to SCC in light water reactor environment: a high-Si stainless steel and a Ni-base weld metal (Alloy 182). The results of the international test programme confirmed that the tapered specimen test methodology could be used to identify a SCC initiation stress threshold, albeit that significant scatter was present in the data. |
|---|
| Ključne besede: | stress corrosion cracking, surface finish impact, tapered tensile specimen, autoclave, accelerated testing, light water nuclear reactor, critical threshold stress |
|---|
| Status publikacije: | Objavljeno |
|---|
| Verzija publikacije: | Objavljena publikacija |
|---|
| Datum objave: | 08.09.2020 |
|---|
| Založnik: | Maney for the Institute of Materials, Minerals, and Mining |
|---|
| Leto izida: | 2020 |
|---|
| Št. strani: | 103-118 |
|---|
| Številčenje: | 56, 2 |
|---|
| PID: | 20.500.12556/DiRROS-16843  |
|---|
| UDK: | 620.1/.2 |
|---|
| ISSN pri članku: | 1743-2782 |
|---|
| DOI: | 10.1080/1478422X.2020.1815460 |
|---|
| COBISS.SI-ID: | 31277059 |
|---|
| Avtorske pravice: | © 2020 The Author(s). Published by Informa UK Limited, trading as Taylor & Francis Group |
|---|
| Opomba: | Nasl. z nasl. zaslona;
Opis vira z dne 6. 10. 2020;
El. članek v PDF formatu;
|
|---|
| Datum objave v DiRROS: | 28.08.2023 |
|---|
| Število ogledov: | 620 |
|---|
| Število prenosov: | 357 |
|---|
| Metapodatki: |    |
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |