| Naslov: | Estimation of the corrosion properties for titanium dental alloys produced by SLM |
|---|
| Avtorji: | ID Kosec, Tadeja (Avtor)
ID Bajt Leban, Mirjam (Avtor)
ID Ovsenik, Maja (Avtor)
ID Kurnik, Matej (Avtor)
ID Kopač, Igor (Avtor) |
|---|
| Datoteke: |  URL - Izvorni URL, za dostop obiščite https://mater-tehnol.si/index.php/MatTech/article/view/519/174
 PDF - Predstavitvena datoteka, prenos (1,97 MB)
MD5: 30EFF1A71291151C30CA8111448771E2
|
|---|
| Jezik: | Angleški jezik |
|---|
| Tipologija: | 1.01 - Izvirni znanstveni članek |
|---|
| Organizacija: |  ZAG - Zavod za gradbeništvo Slovenije
|
|---|
| Povzetek: | Titanium alloys are known for their excellent biocompatible properties. The development of additive-manufacturing technologies has increased the interest in the use of Ti-6Al-4V, produced by selective laser melting (SLM) method, also in dentistry, i.e., prosthodontics and orthodontics. In the present paper, the effect of laser printing parameters in the selective laser melting (SLM) process on the porosity and corrosion behavior of Ti-6Al-4V dental alloy was metallographically and electrochemically studied. All the tests were performed in artificial saliva at 37 °C. Different forms of Ti-6Al-4V alloy were selected: a reference sample, i.e., pre-fabricated milling disc in wrought condition and four different 3D-printed samples made from Ti-6Al-4V powder using the SLM method, one being heat treated. Electrochemical, spectroscopic and hardness measurements were employed in the study. It was shown that the SLM-produced Ti-6Al-4V samples with different printing parameters have similar microstructural and electrochemical properties, while the electrochemical properties of a reference and thermally treated 3D-printed sample were different, most probably due to the change in the microstructure of the alloys. The corrosion properties were related to the microstructural properties as well as to the pore density. |
|---|
| Ključne besede: | Ti-6Al-4V, dental alloys, artificial saliva, selective laser melting, corrosion |
|---|
| Status publikacije: | Objavljeno |
|---|
| Verzija publikacije: | Objavljena publikacija |
|---|
| Datum objave: | 17.08.2022 |
|---|
| Založnik: | Inštitut za kovinske materiale in tehnologije |
|---|
| Leto izida: | 2022 |
|---|
| Št. strani: | str. 429-435 |
|---|
| Številčenje: | Letn. 56, št. 4 |
|---|
| PID: | 20.500.12556/DiRROS-15859  |
|---|
| UDK: | 661.882:616.314 |
|---|
| ISSN pri članku: | 1580-2949 |
|---|
| DOI: | 10.17222/mit.2022.519 |
|---|
| COBISS.SI-ID: | 118977795 |
|---|
| Avtorske pravice: | © MATERIALI IN TEHNOLOGIJE |
|---|
| Opomba: | Nasl. v angl. in slov., besedilo v angl.;
|
|---|
| Datum objave v DiRROS: | 31.05.2023 |
|---|
| Število ogledov: | 658 |
|---|
| Število prenosov: | 288 |
|---|
| Metapodatki: |    |
|---|
|
:
|
Kopiraj citat |
|---|
| | | | Objavi na: |  |
|---|
Postavite miškin kazalec na naslov za izpis povzetka. Klik na naslov izpiše
podrobnosti ali sproži prenos. |