| Title: | Susceptibility of X17CrNi16-2 martensitic stainless steel to hydrogen embrittlement after conventional and deep cryogenic heat treatment |
|---|
| Authors: | ID Bajt Leban, Mirjam (Author)
ID Zajec, Bojan (Author)
ID Podgornik, Bojan (Author)
ID Donik, Črtomir (Author)
ID Jovičević Klug, Patricia (Author)
ID Hren, Miha (Author)
ID Legat, Andraž (Author) |
|---|
| Files: |  URL - Source URL, visit https://www.sciencedirect.com/science/article/pii/S1350630724004497?via%3Dihub
 PDF - Presentation file, download (17,73 MB)
MD5: F3E1D53281F678D3B791A26F7BDC17F1
|
|---|
| Language: | English |
|---|
| Typology: | 1.01 - Original Scientific Article |
|---|
| Organization: |  ZAG - Slovenian National Building and Civil Engineering Institute
|
|---|
| Abstract: | A low carbon/ high chromium martensitic stainless steel, X17CrNi16-2, was heat treated using two different hardening and tempering regimes (1050 ◦ C/480 ◦ C or 980 ◦C/600 ◦C) — promoting either a high strength or high toughness state, respectively and further combined with deep cryogenic treatment (DCT) at 196 ◦C for 24 h. Over recent years DCT has been recognized as a promising technique to improve the properties of steel, predominantly with respect to its tensile strength, toughness and wear resistance. The influence of DCT on the hydrogen embrittlement resistance of martensitic stainless steel has not yet, however, been reported.
A slow strain rate tensile test (SSRT) with simultaneous cathodic hydrogen charging was selected as the method to assess potential susceptibility to hydrogen embrittlement (HE). Relatively low-intensity hydrogen charging, utilizing a constant current density of 0.1 mA/cm2, in a non-corrosive, slightly alkaline buffer solution, led to a clear reduction in the ultimate tensile stress. This reduction, and therefore the HE susceptibility, was more pronounced in the steel with a higher strength (i.e. that subject to the 1050 ◦C/ 480 ◦C heat treatment condition). Furthermore, DCT did not appear to have any impact on the steel’s mechanical properties in the presence of hydrogen. Fractographic analysis showed clear evidence of HE in the hydrogen-charged specimens.
This paper presents results of the SSRT tests and further fractography results, and discusses the impact of conventional and deep cryogenic treatment on HE susceptibility. |
|---|
| Keywords: | martensitic stainless steel, deep cryogenic treatment, hydrogen embrittlement, slow strain rate tensile test |
|---|
| Publication status: | Published |
|---|
| Publication version: | Version of Record |
|---|
| Publication date: | 04.05.2024 |
|---|
| Publisher: | Elsevier |
|---|
| Year of publishing: | 2024 |
|---|
| Number of pages: | str. 1-11 |
|---|
| Numbering: | Vol. 162, [article no.] 108403 |
|---|
| PID: | 20.500.12556/DiRROS-18980  |
|---|
| UDC: | 54 |
|---|
| ISSN on article: | 1873-1961 |
|---|
| DOI: | 10.1016/j.engfailanal.2024.108403 |
|---|
| COBISS.SI-ID: | 194430723 |
|---|
| Copyright: | © 2024 The Authors. |
|---|
| Note: | Received 20 February 2024; Received in revised form 6 April 2024; Accepted 2 May 2024;
Nasl. z nasl. zaslona;
Opis vira z dne 6. 5. 2024;
|
|---|
| Publication date in DiRROS: | 23.05.2024 |
|---|
| Views: | 471 |
|---|
| Downloads: | 399 |
|---|
| Metadata: |    |
|---|
|
:
|
Copy citation |
|---|
| | | | Share: |  |
|---|
Hover the mouse pointer over a document title to show the abstract or click
on the title to get all document metadata. |