| Title: | Rheological behaviors of waste polyethylene modified asphalt binder : Statistical analysis of interlaboratory testing results |
|---|
| Authors: | ID Wang, Di (Author)
ID Baliello, Andrea (Author)
ID Pinheiro, Gustavo (Author)
ID Poulikakos, Lily D. (Author)
ID Tušar, Marjan (Author)
ID Vasconcelos, Kamilla (Author)
ID Kakar, Muhammad Rafiq (Author)
ID Porot, Laurent (Author)
ID Pasquini, Emiliano (Author)
ID Giancontieri, Gaspare (Author)
ID Riccardi, Chiara (Author)
ID Pasetto, Marco (Author)
ID Lo Presti, Davide (Author)
ID Falchetto, Augusto Cannone (Author) |
|---|
| Files: |  URL - Source URL, visit https://www.astm.org/jte20220313.html
 PDF - Presentation file, download (1,19 MB)
MD5: 60C187F987511A2DCF9AB4DC8DB93173
|
|---|
| Language: | English |
|---|
| Typology: | 1.01 - Original Scientific Article |
|---|
| Organization: |  ZAG - Slovenian National Building and Civil Engineering Institute
|
|---|
| Abstract: | This article investigated the effect of waste polyethylene (PE) on the modified asphalt binders’ rheological behavior from a statistical point of view. The interlaboratory testing results from the RILEM Technical Committee 279 Valorization of Waste and Secondary Materials for Roads Task Group 1 were used for this purpose. First, an unaged 70/100 penetration graded neat binder was selected as the reference material. Next, a single 5 % content of waste PE additives (PE-pellets and PE-shreds) was mixed with a 95 % neat binder to prepare two PE modified binders. Then, dynamic shear rheometer–based temperature-frequency sweep tests were performed over a wide range of temperatures and frequencies to evaluate the rheological properties of these three binders. Different rheological behaviors were observed in the isochronal plots at high temperatures. Based on a reproducibility precision requirement proposed for phase angle, 28°C was set as the transition temperature across the rheological behaviors. Next, according to the three rheological behaviors defined in a previous study by the authors, statistical analysis was introduced to identify sensitive rheological parameters and determine the thresholds. Results indicate that the phase angle measured above 28°C and 1.59 Hz can be used as a sensitive parameter to discriminate the three rheological behaviors of PE modified binders. The thresholds among different behaviors were also calculated as an example for phase angle measured at the highest common testing temperature of 70°C. Additional experimental evaluations on more types of PE modified binders, especially at intermediate and high temperatures, are recommended to better understand their influence on the rheological behavior of PE modified binders. |
|---|
| Keywords: | bitumen, polietilen, reologija, medlaboratorijska primerjava |
|---|
| Publication status: | Published |
|---|
| Publication version: | Author Accepted Manuscript |
|---|
| Publication date: | 07.02.2023 |
|---|
| Publisher: | American Society for Testing and Materials |
|---|
| Year of publishing: | 2023 |
|---|
| Number of pages: | str. 2199–2209 |
|---|
| Numbering: | Vol. 51, iss. 4 |
|---|
| PID: | 20.500.12556/DiRROS-18215  |
|---|
| UDC: | 620.1/.2 |
|---|
| ISSN on article: | 1945-7553 |
|---|
| DOI: | 10.1520/JTE20220313 |
|---|
| COBISS.SI-ID: | 141915139 |
|---|
| Copyright: | © 2023 by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959 |
|---|
| Note: | Nasl. z nasl. zaslona;
Opis vira z dne 16. 2. 2023;
|
|---|
| Publication date in DiRROS: | 20.02.2024 |
|---|
| Views: | 622 |
|---|
| Downloads: | 285 |
|---|
| Metadata: |    |
|---|
|
:
|
Copy citation |
|---|
| | | | Share: |  |
|---|
Hover the mouse pointer over a document title to show the abstract or click
on the title to get all document metadata. |