Povzetek: The high temperature corrosion at 650°C in the presence of NaCl at atmospheric pressure of AISI 304L, AISI 309, AISI 310S, AISI 314 and AISI 321 austenitic stainless steel was studied. The specimens were cyclically heated in the furnace and immersed in a 3.5% aqueous NaCl solution after cooling for 15 min. After each cycle, the change in mass of the samples was measured. The corroded samples were analysed by SEM /EDX, and the corrosion products were analysed by XRD. The chloride ions react with the steel surface to form porous and poorly adherent oxides and metal chlorides. After the mass increase during the first exposure cycles, spalling of the oxides occurred. The high temperature austenitic stainless steels (AISI 309, AISI 310S, AISI 314) showed less mass loss than conventional austenitic steels (AISI 304L). Surprisingly, the stainless steel AISI 321 showed a similar low weight loss after the cyclic test as AISI 309, but a detailed analysis of the exposed surfaces after the test showed a similar corrosion attack as for AISI 304. After the cyclic test at high temperature in the presence of NaCl, a higher concentration of Cr and Ni definitely improves the corrosion resistance under the present conditions, but a certain addition of Si is even more obvious.
Ključne besede: austenitic stainless steel, high temperature corrosion, NaCl, exhaust systems, open access
Objavljeno v DiRROS: 31.05.2023; Ogledov: 280; Prenosov: 177
Celotno besedilo (1,53 MB)
Gradivo ima več datotek! Več...

Povzetek: Various coatings have been developed and explored to protect bronze surfaces against the uncontrolled formation of different corrosion products when exposed to outdoor environments. In this research, the surfaces of artificially-formed oxidized bronze patinas (OB), consisting of Cu2O, were covered with either a single-component (fluoroacrylate, FA or methacryloxypropyl-trimethoxysilane, MS) or multi-component (a mixture of FA and MS, FA-MS) fluoropolymer coating and investigated. Variations in the concentration of each component in the coating were studied. Electrochemical tests were performed to determine the corrosion protection efficiency, followed by detailed surface analyses of the OBs, both uncoated and covered with single and multi-component coatings. A variety of investigative methods were used, including focused ion beam scanning electron microscopy (FIB-SEM), X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and time-of-flight secondary ion mass spectrometry (ToF-SIMS). The coating made from a combination of FA and MS resulted in a very high protection efficiency. Despite the increased hydrophilicity of the single MS component, however, it was shown to efficiently protect the oxidized bronze surface. The FA-MS systems showed high hydrophobicity, but no improvement was measured in the efficiency of the corrosion protection when it was compared to the coating that contained 10% MS. According to XPS and ToF-SIMS imaging, the FA component of the FA-MS coating was not present only on the uppermost surface of the coating but throughout the whole coating, which could affect its corrosion protection efficiency.
Ključne besede: bronze, Cu2O layer on bronze, fluoropolymer coating, protection efficiency, surface spectroscopy
Objavljeno v DiRROS: 30.05.2023; Ogledov: 346; Prenosov: 183
Celotno besedilo (8,49 MB)
Gradivo ima več datotek! Več...

Povzetek: The aim of this study was to compare corrosion resistance and ion release in CoCr dental alloys with identical chemical compositions produced using different technologies (SLM – selective laser melting and milling from cast blocks) and heat treatment (SLM parts only). The corrosion properties were tested in artificial saliva, artificial saliva with fluoride ions, and artificial saliva with added lactic acid to simulate inflammations. The study included electrochemical tests, microstructural investigation and ion release tests in the three different environments for a total of 42 days. The best performance of CoCr as a result of potentiodynamic polarization was observed in the artificial saliva with added lactic acid, which is in contradiction with the highest ion release measured from all the materials tested and electrochemical impedance spectroscopy that showed a deterioration of the passive layer in an acidic environment. Microstructural investigation revealed that different phases precipitated by heat treatment trigger increased release of Mo and W ions. The printing method does not raise critically ion release from CoCr alloy, while the state of the surface greatly impacts the extent of the ion release. This study demonstrates the importance of an interdisciplinary approach to the study of corrosion and biocompatibility in dental alloys.
Ključne besede: CoCr dental alloy, selective laser melting, corrosion, ion release, artificial saliva
Objavljeno v DiRROS: 29.05.2023; Ogledov: 344; Prenosov: 290
Celotno besedilo (9,28 MB)
Gradivo ima več datotek! Več...

Povzetek: Laser texturing is a process that alters a material’s surface properties by modifying its morphology, which can improve properties like adherence, wettability, thermal and electrical conductivity and friction. Here, the effect of laser texturing was studied on an alpha-beta titanium alloy (Ti6Al4V) biomedical material. Two types of patterned surfaces, cross-hatch with varying scan-line separations, Dx = 100, 180 and 280 μm and dimples of 200 μm size, were prepared on the surface of alpha-beta titanium alloy by laser technology. Prepared samples were characterised for their surface properties, such as corrosion, wear-induced corrosion, friction and wettability. Electrochemical and tribocorrosion properties in a physiological solution were studied on the samples with different texture densities of cross-hatch pattern and dimples and compared to the as-received alpha-beta titanium alloy surface. Corrosion rate decreased for laser-textured samples, especially for cross-hatch texture (down to 1 μm/year for Dx = 180 μm) when compared to the as-received alpha-beta titanium alloy surface due to the changed laser-induced surface film and wetting properties. Friction coefficient slightly decreased for all laser-textured surfaces, most noticeably for cross-hatch patterns, from 0.38 (as-received) down to 0.34 (Dx = 180 and 280 μm). The main contribution to total wear in physiological solution increased due to the mechanical wear, which is governed by the removal of the surface oxide layer induced by laser texturing.
Ključne besede: TiAIV, laser texturing, tribocorrosion, open access
Objavljeno v DiRROS: 17.05.2023; Ogledov: 294; Prenosov: 120
Celotno besedilo (2,19 MB)
Gradivo ima več datotek! Več...

Ključne besede: children, sixth grade, moderate to vigorous intensity, accelerometer
Objavljeno v DiRROS: 02.03.2023; Ogledov: 321; Prenosov: 167
Celotno besedilo (384,27 KB)
Gradivo ima več datotek! Več...