Fibre reinforced alkali-activated rock wool
Majda Pavlin, Barbara Horvat, Vilma Ducman, 2022, published scientific conference contribution

Abstract: Mineral wool, i.e. rock and glass wool, represents considerable challenge after its functional-time runs out due to its small density leading to large volume consumption during transport and in landfills where it usually ends. Because rock wool is mineralogically and chemically a promising precursor material for alkali-activation, it was milled from few centimetres-decimeters long fibres to micron-sized fibres. Since fibres in alkali-activated materials generally show an increase in mechanical strength, especially the bending strength, 1 m% of additional fibres (basalt, cellulose (2 types), glass, polypropylene, polyvinyl alcohol and steel fibres) was used in the alkali mixture, that was curred at 40 °C for 3 days. Time dependence of the mechanical strengths of alkali- activated materials with and without additional fibres was followed. Maximal increase of compressive and bending strength after 28 days was reached with polypropylene fibres, i.e. it was 20% and 30% higher than compressive and bending strength of alkali- activated material without additional fibres respectively.
Keywords: secondary raw material, alkali activated material, foaming, homogenization, mechanical strength
Published in DiRROS: 21.12.2023; Views: 233; Downloads: 79
.pdf Full text (8,39 MB)
This document has many files! More...

2.
Influence of homogenization of alkali-activated slurry on mechanical strength
Barbara Horvat, Mark Češnovar, Katja Traven, Majda Pavlin, Katja Koenig, Vilma Ducman, 2022, published scientific conference contribution

Abstract: Alkali-activated materials are promising materials for the construction industry due to the accessibility of the precursors, which are mainly secondary industrial by-products, and their cost- effective and energy-efficient production. Although these materials are not new, some of the parameters in the technological process are not yet fully understood and tested. Therefore, in this paper in the means of mechanical strength, the preparation of alkali-activated pastes by using a three-roll mill homogenization method is discussed. The influence of homogenization of alkali- activated slurry has been evaluated on different waste materials (fly ash, fly ash with metakaolin, slag mixture (electric arc furnace slag and ladle slag), glass wool, waste green ceramics), which are treated with different alkali activators (NaOH, commercial sodium silicate solution, laboratory-produced alkali activators based on waste cathode- ray tube glass) with different curing regimes (60 °C and 70 °C) and different drying methods (drying at room temperature, drying at 105 °C). The viscosity of the slurry before homogenization was higher than after homogenization, the distribution of elements was more uniform and the compressive strength higher in all homogenized alkali activated materials, regardless of other parameters.
Keywords: secondary raw material, alkali activated material, foaming, homogenization, mechanical strength