Use of fly ash and phosphogypsum for the synthesis of belite-sulfoaluminate clinkerSabina Dolenec,
Lea Žibret,
Emilija Fidanchevska,
V. Jovanov,
Biljana Angjusheva,
Vilma Ducman, 2019, izvirni znanstveni članek
Povzetek: Fly ash and phosphogypsum were used as Naturally Occurring Radioactive Materials (NORM) by-products for the synthesis of belite-sulfoaluminate clinkers. The influence of raw mixture composition and firing temperature was investigated. Clinkers and cements were examined by X-ray powder diffraction and scanning electron microscopy with energy dispersive X-ray spectroscopy. The compressive strength of the cements was determined after 28 days. Clinker phases identified included ye’elimite, ß-phase of belite, ternesite and gehlenite, while the main hydration product of the cement pastes was ettringite. The results showed that belite-sulfoaluminate cements can be fabricated with a compressive strength of 45.9 N/mm2 by firing the raw mixture (70 wt.% marl, 10 wt.% bauxite and 20 wt.% phosphogypsum) at a temperature of 1320°C/1h.
Ključne besede: clinker, microstructure, fly ash, gypsum, calcium sulphoaluminate
Objavljeno v DiRROS: 27.10.2023; Ogledov: 595; Prenosov: 282
Celotno besedilo (2,01 MB)
Gradivo ima več datotek! Več...