Povzetek: The aim of the study was to quantify planned doses to the heart and specific cardiac substructures in free-breathing adjuvant three-dimensional radiation therapy (3D-CRT) and tangential intensity modulated radiotherapy (t-IMRT) for left-sided node-negative breast cancer, and to assess the differences in planned doses to organs at risk according to patients% individual anatomy, including breast volume. Patients and methods. In the study, the whole heart and cardiac substructures were delineated for 60 patients using cardiac atlas. For each patient, 3D-CRT and t-IMRT plans were generated. The prescribed dose was 42.72 Gy in 16 fractions. Patients were divided into groups with small, medium, and large clinical target volume (CTV). Calculated dose distributions were compared amongst the two techniques and the three different groups of CTV. Results. Mean absorbed dose to the whole heart (MWHD) (1.9 vs. 2.1 Gy, P < 0.005), left anterior descending coronary artery mean dose (8.2 vs. 8.4 Gy, P < 0.005) and left ventricle (LV) mean dose (3.0 vs. 3.2, P < 0.005) were all significantly lower with 3D-CRT technique compared to t-IMRT. Apical (8.5 vs. 9.0, P < 0.005) and anterior LV walls (5.0 vs. 5.4 Gy, P < 0.005) received the highest mean dose (Dmean). MWHD and LV-Dmean increased with increasing CTV size regardless of the technique. Low MWHD values (< 2.5 Gy) were achieved in 44 (73.3%) and 41 (68.3%) patients for 3D-CRT and t-IMRT techniques, correspondingly. Conclusions. Our study confirms a considerable range of the planned doses within the heart for adjuvant 3D-CRT or t-IMRT in node-negative breast cancer. We observed differences in heart dosimetric metrics between the three groups of CTV size, regardless of the radiotherapy planning technique.
Ključne besede: breast cancer, radiotherapy, 3D-CRT
Objavljeno v DiRROS: 16.07.2024; Ogledov: 2; Prenosov: 1
Celotno besedilo (544,83 KB)

Povzetek: We investigated micro-threaded stem taper surface and its impact on premature failures, aseptic loosening, and infection in cementless hip endoprostheses. Our study focused on the fretting, and crevice corrosion of micro-threaded tapers, as well as the characterization of the microstructure and surface properties of two new and three retrieved Zweymüller stem tapers. The retrieved samples were selected and examined based on the head–stem taper interface being the sole source of modularity with a metallic component, specifically between the Ti alloy taper stem and the ceramic head. To determine the surface chemistry and microstructures of both new and retrieved hip endoprostheses stem taper titanium alloy, scanning -electron microscopy (SEM) was employed for morphological and microstructural analyses. Energy dispersive spectroscopy (EDS) was utilized for characterizing chemical element distribution, and electron backscattered diffraction (EBSD) was used for phase analysis. The roughness of the micro-threated stem tapers from different manufacturers was investigated using an optical profilometer, with standard roughness parameters Ra (average surface roughness) and Rz (mean peak to valley height of the roughness profile) being measured. Electrochemical studies revealed no fretting corrosion in retrieved stem tapers with ceramic heads. Consequently, three retrieved tapers and two new ones for comparison underwent potentiodynamic measurements in Hank’s solution to determine the corrosion rate of new and retrieved stem taper surfaces. The results showed a low corrosion rate for both new and prematurely failed retrieved samples due to aseptic loosening. However, the corrosion rate was higher in infected and low-grade infected tapers. In conclusion, our study suggests that using ceramic heads reduces taper corrosion and subsequently decreases the incidence of premature failures in total hip arthroplasty.
Ključne besede: total hip arthroplasty, stem micro-threaded taper, taper surface morphology, microstructure, corrosion, Ti implant alloy
Objavljeno v DiRROS: 06.06.2024; Ogledov: 149; Prenosov: 136
Celotno besedilo (8,47 MB)
Gradivo ima več datotek! Več...

Ključne besede: rapid antigen tests, recycling, characterization, nanogold, plastic
Objavljeno v DiRROS: 28.02.2024; Ogledov: 332; Prenosov: 124
Celotno besedilo (1,74 MB)
Gradivo ima več datotek! Več...

Povzetek: In this paper, we present the mechanisms of premature fracture of modular neck stems in two case studies: (I) when the neck and stem are both made of the same Ti6Al4V alloy, and (II) when the neck and stem are made from two different alloys, CoCrMo and Ti6Al4V alloy. Our study integrates two orthopedic patients who have undergone primary uncemented THA for usual indications in two orthopedic centers (Community Health Centre and University Medical Centre). Both centers are part of the national public health care system. Both surgeries were performed by two skilled orthopedic surgeons with more than 10 years of experience in THA. The survivorship of the modular neck of cast CoCrMo alloy was 24 months. The survivorship of the modular neck from Ti6Al4V alloy was 84 months. Multivariate analyses were performed to assess the differences in the fretting, corrosion, and fatigue of the two prematurely failed modular neck stems: stereo light microscopy (SLM), scanning electron microscopy (SEM), X-ray energy-dispersive spectroscopy (EDS), and electron backscatter diffraction (EBSD). Patient demographic information, including sex, age, body mass index, survivorship of implants, and reason for the revision, was collected from medical records. We found that fretting and fatigue occurred on both neck-stem retrievals due to additional galvanic corrosion, but the CoCrMo/Ti6Al4V alloy system suffered more corrosion due to additional galvanic corrosion and fractured earlier than the Ti6Al4V/Ti6Al4V metal alloy system. Both metallic alloy systems used in this application are known to be highly corrosion-resistant, but the bio-tribo-corrosion processes need to be understood in detail and characterized so that appropriate improvements in design and materials can be made.
Ključne besede: total hip arthroplasty, modular neck, Ti6Al4V alloy, CoCrMo alloy, corrosion
Objavljeno v DiRROS: 07.02.2024; Ogledov: 359; Prenosov: 197
Celotno besedilo (5,12 MB)
Gradivo ima več datotek! Več...

Ključne besede: endoprosthesis failure, corundum, cytokines, reactive oxygen species, lipid droplets