Povzetek: The design process of concrete structures is carried out using standards and guidelines, while the durability predictions of concrete structures is supported only with exposure classes and experience-based requirements. To improve durability predictions of the carbonation resistance of concrete, a numerical model is being developed within the Horizon 2020 project EnDurCrete, coupling the rate of carbonation, and the drying rate. To verify the numerical model, an accelerated carbonation study was carried out. Experiments were conducted on mortars incorporating a novel CEM II/C (S-LL) cement, developed within the EnDurCrete project, and a commercially available reference cementCEM II/A-S. EnDurCrete mortars (EnM) and reference mortars (RefM) were prepared with water-cement ratios of 0.6 and 0.5 (denoted with label extensions -06 and -05). Visual assessments and thermogravimetric analysis (TGA) were used to measure the carbonation rates, which were found to be ~1.0 mm day-0.5 in EnM-06 and ~0.6 mm day-0.5 in RefM-06, while in EnM-05 and RefM-05 the values were ~0.7 and ~0.2 mm day-0.5 respectively. Additionally, TGA shows that the initial portlandite (CH) content is ~1.5 wt% in EnM-06 as opposed to ~3.0 wt% in RefM-06. The difference in the initial CH content in the two hydrated binders might explain the difference in their carbonation rate. During the moisture transport experiments a gravimetric method was used to determine mass changes as specimens underwent drying and resaturation with and without CO2 present. The drying led to a decrease in mass, but in the presence of CO2 this mass loss was compensated by the mass gain due to uptake of CO2 during carbonation. The resaturation experiments indicate an increase in the suction porosity in the carbonated samples compared to the non-carbonated samples.
Ključne besede: concrete, absorption of water, carbonation, durability assessment, model verification
Objavljeno v DiRROS: 25.01.2024; Ogledov: 154; Prenosov: 110
Celotno besedilo (9,29 MB)
Gradivo ima več datotek! Več...

Povzetek: The aim of RILEM TC 247-DTA Durability Testing of Alkali-Activated Materials is to identify and validate methodologies for testing the durability of alkali-activated concretes. To underpin the durability testing work of this committee, five alkali-activated concrete mixes were developed based on blast furnace slag, fly ash, and flash-calcined metakaolin. The concretes were designed with different intended performance levels, aiming to assess the capability of test methods to discriminate between concretes on this basis. A total of fifteen laboratories worldwide participated in this round robin test programme, where all concretes were produced with the same mix designs, from single-source aluminosilicate precursors and locally available aggregates. This paper reports the mix designs tested, and the compressive strength results obtained, including critical insight into reasons for the observed variability in strength within and between laboratories.
Ključne besede: alkali-activated materials (AAM), mechanical properties, test method, Rilem TC, durability
Objavljeno v DiRROS: 14.09.2023; Ogledov: 229; Prenosov: 133
Celotno besedilo (431,19 KB)
Gradivo ima več datotek! Več...

Povzetek: The demand for construction timber is continuously increasing, due to its favourable characteristics. However, the adequate protection of wood is key to its successful use, as it is flammable and susceptible to biodegradation. Given that thermal modification enhances the durability of wood, and mineralisation with CaCO3 considerably improves its fire properties, it is worth considering the combined effects of the two methods. European beech (Fagus sylvatica) was selected to determine the effects of a) thermal modification, b) mineralisation through the in-situ formation of CaCO3, and c) a combination of the two procedures, on resistance to decay fungi, reaction to fire and the mechanical properties of the wood. Microscopic analysis and comparisons of the samples before and after exposure to fungi were also conducted. Mineralised wood generally had a slightly alkaline pH value and higher equilibrium moisture content, while thermal modification lowered the equilibrium moisture content. The present study demonstrated the combined effect of thermal modification and mineralisation: the best response to fire as well as resistance to fungi was achieved when the two treatments were combined. Results from the Brinell hardness and three-point bending tests indicate that both modification procedures can slightly impair the mechanical properties of the wood.
Ključne besede: wood, protection, durability, mechanical properties
Objavljeno v DiRROS: 12.07.2023; Ogledov: 329; Prenosov: 243
Celotno besedilo (3,26 MB)
Gradivo ima več datotek! Več...

Povzetek: The development of non-biocidal and environmentally friendly systems to protect wood against biological decay has become a high priority in recent years. In the present study the impact of an innovative modification procedure, combining two environmentally friendly modification methods: thermal modification and mineralisation, using an aqueous solution of calcium acetoacetate as a precursor, on the fungal durability of wood was evaluated. European beechwood (Fagus sylvatica) and Norway sprucewood (Picea abies) were selected as model wood species. Wood samples were treated using either a single or combination of both methods and exposed to four different fungi: Gloeophyllum trabeum, Rhodonia placenta, Trametes versicolor and Pleurotus ostreatus. The effect of the different modifications on moisture content, dynamic vapour sorption, contact angle and pH value was also evaluated. Overall, the highest durability against Rhodonia placenta, Trametes versicolor and Pleurotus ostreatus was achieved through thermal modification in both wood species, while the combination of mineralisation and thermal modification has a synergistic effect against degradation by Gloeophyllum trabeum. In the case of beechwood the mass loss decreased from 41% for native to 6% for combined modified samples. We proved that the effectiveness of different treatment against fungal decay of wood were in strong dependence of their moisture content, dynamic vapour sorption, contact angle and pH values. The role of fungi on the morphology of the wood and on crystal structure of formed carbonate was investigated using SEM-EDS analysis.
Ključne besede: thermal modification, wood mineralization, fungal durability, environmentally friendly modification methods
Objavljeno v DiRROS: 20.06.2023; Ogledov: 323; Prenosov: 374
Celotno besedilo (3,55 MB)
Gradivo ima več datotek! Več...