1.
Particle size manipulation as an influential parameter in the development of mechanical properties in electric arc furnace slag-based AAM
Katja Traven, Mark Češnovar, Vilma Ducman, 2019, izvirni znanstveni članek

Povzetek: Alkali-activated materials (AAM) have gained recognition as a promising alternative to technical ceramic and building materials owing to the lower energy demands for production and the potential to use slag as a precursor. In the present study, five sets of slag-based AAM pastes were prepared with different particle sizes (fractions d < 63, 63 < d < 90, and 90 < d < 125 μm in different mass ratios) under the same curing regime and using a fixed precursor to activator (water) mass ratio. Precursors and the hardened AAM are evaluated using BET, XRD, XRF, SEM, FTIR, reactivity of precursors by leaching, and mercury intrusion porosimetry (MIP). Chemical analysis indicated only marginal differences among the different-sized fractions of input materials, whereas the BET surface area and reactivity among the precursors differed significantly-smaller particles had the largest surface area, and thus, higher reactivity. The mineralogical differences between the precursors and hardened AAM were negligible. The results revealed that compressive strength was significantly influenced by particle size, i.e., a threefold increase in strength when the particle size was halved. Microstructural evaluation using MIP confirmed that the porosity was the lowest in AAM with the smallest particle size. The low porosity and high reactivity of the fine fractions led to the highest compressive strength, confirming that manipulation of particle size can significantly influence the mechanical properties.
Ključne besede: alkalijsko aktivirani materiali, žlindra iz obločne peči, mehanska aktivacija, mehanske lastnosti, poroznost, alkali-activated materials (AAM), electric arc furnace steel slag, mechanical activation, mechanical properties, porosity
Objavljeno v DiRROS: 22.11.2023; Ogledov: 203; Prenosov: 112
.pdf Celotno besedilo (2,26 MB)
Gradivo ima več datotek! Več...

2.
Influence of microwaves in the early stage of alkali activation on the mechanical strength of alkali-activated materials
Barbara Horvat, Majda Pavlin, Vilma Ducman, 2023, izvirni znanstveni članek

Povzetek: This study focuses on the influence of microwave irradiation dosimetry on alkali-activated slurry in its early stages. The impact on the chemistry and mineralogy along with the mechanical properties were evaluated by changing the power of microwaves and their duration of exposure. This influenced the dissolution of amorphous content, diffusion, and self-assembly into an aluminosilicate network. The precursors used in this study were metakaolin, a non-waste material commonly used in geopolymerisation technology, and local fly ash and ladle furnace slag as secondary materials. Furthermore, they were chemically and mineralogically analysed, and their mixtures with NaOH and Na-water glass provided the optimal ratio of the amount of elements obtained using the pre-calculation approach. However, the potential extra addition of water was experimentally determined to allow complete wetting of the material and solid workability during moulding. Using Fourier-transform infrared spectroscopy, the influence of water was further investigated in alkali-activated slag and fly ash irradiated with microwaves, which resulted in the highest values of mechanical strength in the dosimetry-mapping part of the analysis. In addition to the time dependence of the expected mechanical strength on the ageing of the alkali- activated material, the synthesised material exhibited a significant dependence on the dose of microwave irra- diation, which was different for every precursor as well as every mixture with different chemistries.
Ključne besede: odpadni material, alkalijska aktivacija, obsevanje z mikrovalovi, mehanska trdnost, waste material, alkali activation, microwave irradiation, mechanical strength
Objavljeno v DiRROS: 12.07.2023; Ogledov: 330; Prenosov: 245
.pdf Celotno besedilo (8,99 MB)
Gradivo ima več datotek! Več...

3.
The preparation and characterization of low-temperature foams based on the alkali activation of waste stone wool
Majda Pavlin, Barbara Horvat, Mark Češnovar, Vilma Ducman, 2022, izvirni znanstveni članek

Povzetek: Waste mineral wool represents a huge amount of construction and demolition waste that is still not adequately returned into the value chain but needs to be landfilled. In the present study, waste stone wool (SW) was evaluated for the preparation of alkali-activated foams. For this purpose SW was milled and sieved below 63 μm, then the activator (sodium silicate) and different amounts of foaming agent (hydrogen peroxide, H2O2), varying between 1 wt% and 3 wt%, were added to the slurry and cured in moulds at an elevated temperature (70 ◦ C) for three days. In this way, foamed, highly porous materials were obtained whose density and mechanical properties were influenced by the amount of foaming agent used. The densities obtained ranged between 1.4 and 0.5 g/cm3, with corresponding mechanical properties of between 12.6 and 1.5 MPa and total porosities in the range 37.8–78.6%, respectively. In the most porous samples with the total porosity of 78.6%, a thermal conductivity of 0.092 W/(m∙K) was confirmed. The study confirmed the suitability of waste mineral wool (in our case SW) as a precursor for alkali-activated foams with potential use in the construction sector or other industrial applications.
Ključne besede: alkali activation, waste mineral wool, mechanical strength, open access, alkalijska aktivacija, odpadna volna, SEM, XRF, XRD, mehanska trdnost, odprti dostop
Objavljeno v DiRROS: 19.06.2023; Ogledov: 238; Prenosov: 181
.pdf Celotno besedilo (9,47 MB)
Gradivo ima več datotek! Več...

4.
5.
Akutni učinki kognitivnega treninga na kortikospinalo in mišično aktivacijo : končno raziskovalno poročilo
Armin Paravlić, 2021, končno poročilo o rezultatih raziskav

Ključne besede: šport, treningi, mišice, aktivacija mišic, kortikospinala, aktivacija kortikospinale
Objavljeno v DiRROS: 21.12.2021; Ogledov: 780; Prenosov: 237
.pdf Celotno besedilo (372,23 KB)

6.
Identifikacija vrste mišične utrujenosti po športnem naporu : končno poročilo o rezultatih raziskave
Boštjan Šimunič, Katarina Puš, Jure Urbanc, Aleš Holobar, Miloš Kalc, 2021, končno poročilo o rezultatih raziskav

Ključne besede: šport, napor, mišice, aktivacija mišic, utrujenost
Objavljeno v DiRROS: 20.12.2021; Ogledov: 864; Prenosov: 386
.pdf Celotno besedilo (949,44 KB)
Gradivo ima več datotek! Več...

Iskanje izvedeno v 0.24 sek.
Na vrh