Influence of curing / drying methods including microwave heating on alkali activation of waste casting coresBarbara Horvat,
Vilma Ducman, 2021, objavljeni znanstveni prispevek na konferenci
Povzetek: Within previous investigation alkali activation of waste casting cores at room temperature did not give promising results, i.e. when the precursor was gently ground and sieved below 600 %m the alkali activated material fell apart at demolding, and when the precursor was ground below 90 %m, the alkali activated material did not solidify in more than 2 years. , Therefore different drying/curing methods were applied to enhance the reaction. Waste casting cores were prepared in two granulations (sieved below 600 %m and below 90 %m), activated with Na -water glass and 10 M NaOH, cured at different temperatures (70 °C and room temperature), and subsequently cured/dried at three different conditions: room temperature, 110 °C, and irradiated with microwaves. The highest compressive strength, 25 MPa, was gained with subsequent curing/drying at 110 °C. The lowest density, 0.5 kg/l, with compressive strength above 3 MPa, was achieved with subsequent curing/drying with microwaves .
Ključne besede: waste casting cores, alkali activation, curing, drying, microwaves, mechanical strength
Objavljeno v DiRROS: 22.01.2024; Ogledov: 544; Prenosov: 352
Celotno besedilo (9,29 MB)
Gradivo ima več datotek! Več...