Lightweight aggregates made from fly ash using the cold-bond process and their use in lightweight concreteAna Frankovič,
Violeta Bokan-Bosiljkov,
Vilma Ducman, 2017, izvirni znanstveni članek
Povzetek: Aggregates made from fly ash have been developed by means of the cold-bonding process, with the addition of Portland cement as a binder at (10, 20, and 30) % of mass fractions, and by pouring the mixtures into moulds. After curing for 28 d the samples were processed into aggregate by crushing and sieving. An aggregate containing a weight percentage of 10 % of cement was additionally produced by pelletization on a granulating plate. The density, water-adsorption capacity, porosity, compressive strengths, and frost resistance of the samples were determined. The aggregates prepared by both routes were then used to make concrete samples, whose properties were then compared to those of conventional concrete made using limestone aggregate. The compressive strength of the concrete made with the granulated aggregate reached 16.0 MPa after 28 d, whereas that of the concrete made with crushed aggregate amounted to 24.1 MPa, and that of the conventional concrete was 34.6 MPa.
Ključne besede: fly ash, lightweight aggregates, density, compressive strength, frost resistance
Objavljeno v DiRROS: 14.08.2024; Ogledov: 1089; Prenosov: 655
Celotno besedilo (1,65 MB)
Gradivo ima več datotek! Več...