1.
Influence of ammonium polyphosphates and 2,4,6-triamino-1,3,5-triazine on the mechanical-physical properties of polyurethane and alkali-activated materials
Branka Mušič, Barbara Horvat, 2024, objavljeni znanstveni prispevek na konferenci

Povzetek: In building constructions, the tendency towards an ever-better material directs us to composite materials. In this work, we prepared an organic-organic and organic-inorganic composite material by incorporating fire retardants, ammonium polyphosphates, and 2,4,6-triamino-1,3,5-triazine, into a polyurethane network and an aluminosilicate network (ASN) of alkali-activated material. Polyurethane foams (PUR) are well-known materials that, due to their properties, such as low weight-to-strength ratio, low electrical and thermal conductivity, flexibility, and relatively simple preparation process, are used in various industries, also in the construction industry, e.g., for thermal insulation of windows and doors or fixing and sealing joinery. Opposite, the ASN of alkali-activated metakaolin, successfully paves the way for new applications, such as high-temperature protection. In this paper, these interactive properties of prepared composites are studied using thermal testing and mechanical analysis. It was found that inhibitors significantly increase the fire resistance of PUR systems while they slightly reduce the mechanical properties. Incorporating polymer flame retardant into ASN in building products, such as façade panels , can decrease the mechanical properties but can offer the non-flammable building envelope not get heated from burning surroundings, i.e., not becoming a convection heat source, but rather represent a fire-distinguisher for flammable materials.
Ključne besede: flame retardants, polyurethane, alkali activated material, metakaolin, microwave irradiation, mechanical strength
Objavljeno v DiRROS: 12.03.2024; Ogledov: 629; Prenosov: 466
.pdf Celotno besedilo (2,52 MB)
Gradivo ima več datotek! Več...

2.
Thermal insulation and flammability of composite waste polyurethane foam encapsulated in geopolymer for sustainable building envelope
Barbara Horvat, Nataša Knez, Uroš Hribar, Jakob Koenig, Branka Mušič, 2024, izvirni znanstveni članek

Povzetek: Polyurethane foam (PUR) is a lightweight, thermally insulating, widely used, and highly flammable material that has after its use an adverse effect on the environment, i.e., PUR disposal is considered hazardous. Its flammability can be mitigated using various fire retardants, but they do not change the hazardous nature of waste PUR. Therefore, in the current study, waste PUR with and without flame retardants based on N and P was incorporated into a geopolymer, the alkali-activated material (AAM) based solely on metakaolin, to evaluate the potential recycling route of waste PUR while taking into account its flammability, so it can enter safely into the circular economy through the building industry. To enhance the mechanical properties of the composite, a fresh mixture was irradiated with microwaves. However, the irradiation of geopolymer containing PUR negatively influenced mechanical performance, which led to the evaluation of the behaviour of the complex dielectric constant of PUR and fire retardants. Materials and composites were evaluated regarding their chemistry, mineralogy, microstructure, and porosity to connect the structure with extrinsic properties like geometrical density, thermal conductivity, and fire properties. Nonetheless, positive influences of PUR being encapsulated in the geopolymer were lowered density (from 1.8 to 1.6 kg/l) and improved thermal insulation ability (from 940 to 860 mW/(m·K)) of the composites: with the inclusion of <5 % of PUR, thermal insulation improved by nearly 10 %. However, the contribution of PUR to the composite originated from its skeleton, which has more than 15 times bigger geometrical density (0.81 kg/l) compared to the density of the skeleton (0.047 kg/l). This offers an open field for further advancements of thermal properties, but would also lead to a decrease of the compressive strength, which was already lowered from 90 MPa for 30 % with <5 % of added grated PUR. Furthermore, the flammable nature of PUR and its other drawbacks can be controlled by permanent embedding in the noncombustible structure of geopolymer, making the envelope of sustainable buildings green and safer. Overall, including grated waste PUR in geopolymer represents a promising, easy, cost-effective recycling path with low energy consumption, where the composite cannot develop fire on a scale of pure PUR, even in the worst-case scenario, but only if the composite is designed in a way, that flammable materials cannot join flames during their combustion. This paper gives prospects to other flammable waste materials to be safely used in the circular economy, and to porous materials to shape properties of the composite by their intrinsic and/or extrinsic properties.
Ključne besede: waste polyurethane foam, polymeric flame retardants, alkali activated material, metakaolin, microwave irradiation, thermal-fire behaviour, mechanical strength
Objavljeno v DiRROS: 01.03.2024; Ogledov: 947; Prenosov: 889
.pdf Celotno besedilo (29,74 MB)
Gradivo ima več datotek! Več...

3.
PUR in geopolymer
Barbara Horvat, Nataša Knez, Uroš Hribar, Jakob Koenig, Branka Mušič, 2024, zaključena znanstvena zbirka raziskovalnih podatkov

Povzetek: The dataset supports the results shown in the tables and figures in the article entitled “Thermal insulation and flammability of composite waste polyurethane foam encapsulated in geopolymer for sustainable building envelope” (doi: 10.1016/j.jclepro.2024.141387). It contains measurements of fire-behaviour characteristics, thermal conductivity, the behaviour of the material in the electromagnetic field in relation to the frequency, mechanical and structural evaluation, as well as chemical and mineralogical analysis.
Ključne besede: measurements, waste polyurethane foam, polymeric flame retardants, alkali activated material, metakaolin, microwave irradiation, thermal-fire behaviour, mechanical strength
Objavljeno v DiRROS: 20.02.2024; Ogledov: 806; Prenosov: 302
.xlsx Raziskovalni podatki (2,51 MB)