1. RILEM TC 247-DTA round robin test : mix design and reproducibility of compressive strength of alkaliactivated concretesJohn L. Provis, Kamel Arbi, Susan A. Bernal, Dali Bondar, Anja Buchwald, Arnaud Castel, Sundararaman Chithiraputhiran, Martin Cyr, Alireza Dehghan, Katja Dombrowski-Daube, Ashish Dubey, Vilma Ducman, Gregor J. G. Gluth, Sreejith Nanukuttan, Karl Peterson, Francisca Puertas, Arie van Riessen, Manuel Torres-Carrasco, Guang Ye, Yibing Zuo, 2019, izvirni znanstveni članek Povzetek: The aim of RILEM TC 247-DTA Durability Testing of Alkali-Activated Materials is to identify and validate methodologies for testing the durability of alkali-activated concretes. To underpin the durability testing work of this committee, five alkali-activated concrete mixes were developed based on blast furnace slag, fly ash, and flash-calcined metakaolin. The concretes were designed with different intended performance levels, aiming to assess the capability of test methods to discriminate between concretes on this basis. A total of fifteen laboratories worldwide participated in this round robin test programme, where all concretes were produced with the same mix designs, from single-source aluminosilicate precursors and locally available aggregates. This paper reports the mix designs tested, and the compressive strength results obtained, including critical insight into reasons for the observed variability in strength within and between laboratories. Ključne besede: alkali-activated materials (AAM), mechanical properties, test method, Rilem TC, durability Objavljeno v DiRROS: 14.09.2023; Ogledov: 574; Prenosov: 311 Celotno besedilo (431,19 KB) Gradivo ima več datotek! Več... |
2. RILEM TC 247-DTA round robin test : carbonation and chloride penetration testing of alkali-activated concretesGregor J. G. Gluth, Kamel Arbi, Susan A. Bernal, Dali Bondar, Arnaud Castel, Sundararaman Chithiraputhiran, Alireza Dehghan, Katja Dombrowski-Daube, Ashish Dubey, Vilma Ducman, Karl Peterson, Penny Pipilikaki, Siska L. A. Valcke, Guang Ye, Yibing Zuo, John L. Provis, 2020, izvirni znanstveni članek Povzetek: Many standardised durability testing methods have been developed for Portland cement-based concretes, but require validation to determine whether they are also applicable to alkali-activated materials. To address this question, RILEM TC 247-DTA "Durability Testing of Alkali-Activated Materials" carried out round robin testing of carbonation and chloride penetration test methods, applied to five different alkali-activated concretes based on fly ash, blast furnace slag or metakaolin. The methods appeared overall to demonstrate an intrinsic precision comparable to their precision when applied to conventional concretes. The ranking of test outcomes for pairs of concretes of similar binder chemistry was satisfactory, but rankings were not always reliable when comparing alkali-activated concretes based on different precursors. Accelerated carbonation testing gave similar results for fly ash-based and blast furnace slag-based alkali-activated concretes, whereas natural carbonation testing did not. Carbonation of concrete specimens was observed to have occurred already during curing, which has implications for extrapolation of carbonation testing results to longer service life periods. Accelerated chloride penetration testing according to NT BUILD 443 ranked the tested concretes consistently, while this was not the case for the rapid chloride migration test. Both of these chloride penetration testing methods exhibited comparatively low precision when applied to blast furnace slag-based concretes which are more resistant to chloride ingress than the other materials tested. Ključne besede: alkali-activated materials (AAM), carbonatization, chloride penetration, Rilem TC, durability Objavljeno v DiRROS: 17.08.2023; Ogledov: 570; Prenosov: 434 Celotno besedilo (1014,30 KB) Gradivo ima več datotek! Več... |
3. RILEM TC 247-DTA round robin test : sulfate resistance, alkali-silica reaction and freeze-thaw resistance of alkali-activated concretesFrank Winnefeld, Gregor J. G. Gluth, Susan A. Bernal, Maria Chiara Bignozzi, Lorenza Carabba, Sundararaman Chithiraputhiran, Alireza Dehghan, Sabina Dolenec, Katja Dombrowski-Daube, Ashish Dubey, Vilma Ducman, Yu Jin, Karl Peterson, Stephen Dietmar, John L. Provis, 2020, izvirni znanstveni članek Povzetek: The RILEM technical committee TC 247-DTA ‘Durability Testing of Alkali-Activated Materials’ conducted a round robin testing programme to determine the validity of various durability testing methods, originally developed for Portland cement based-concretes, for the assessment of the durability of alkali-activated concretes. The outcomes of the round robin tests evaluating sulfate resistance, alkali-silica reaction (ASR) and freeze–thaw resistance are presented in this contribution. Five different alkali-activated concretes, based on ground granulated blast furnace slag, fly ash, or metakaolin were investigated. The extent of sulfate damage to concretes based on slag or fly ash seems to be limited when exposed to an Na2SO4 solution. The mixture based on metakaolin showed an excessive, very early expansion, followed by a dimensionally stable period, which cannot be explained at present. In the slag-based concretes, MgSO4 caused more expansion and visual damage than Na2SO4; however, the expansion limits defined in the respective standards were not exceeded. Both the ASTM C1293 and RILEM AAR-3.1 test methods for the determination of ASR expansion appear to give essentially reliable identification of expansion caused by highly reactive aggregates. Alkali-activated materials in combination with an unreactive or potentially expansive aggregate were in no case seen to cause larger expansions; only the aggregates of known very high reactivity were seen to be problematic. The results of freeze–thaw testing (with/without deicing salts) of alkali-activated concretes suggest an important influence of the curing conditions and experimental conditions on the test outcomes, which need to be understood before the tests can be reliably applied and interpreted. Ključne besede: alkali-activated materials/geopolymers, sulphate resistance, alkali silica reactivity, freeze-thaw resistance, Rilem TC Objavljeno v DiRROS: 17.08.2023; Ogledov: 604; Prenosov: 337 Celotno besedilo (560,56 KB) Gradivo ima več datotek! Več... |