1.
Characterization of fly ash alkali activated foams obtained using sodium perborate monohydrate as a foaming agent at room and elevated temperatures
Lidija Korat, Vilma Ducman, 2020, original scientific article

Abstract: Alkali activated foams have been extensively studied in recent years, due to their high performance and low environmental footprint compared to foams produced via other methods. Three types of fly ash differing in chemical and mineralogical composition and specific surface were used to synthesize alkali activated foams. Sodium perborate monohydrate was added as a foaming agent and sodium dodecyl sulphate as a stabilizing agent. Foams were characterized at room temperature and after exposure to an elevated temperature (1,000 °C). Densities from 1.2 down to 0.3 g/cm 3 were obtained, depending on the type of fly ash and quantity of foaming agent added. Correspondingly, compressive strength ranged from 1 to 6 MPa. Comparing all three fly ashes the most favorable results, in terms of density and corresponding compressive strength, were achieved from the fly ash with the highest amounts of SiO 2 and Al2 O 3 , as well as the highest amorphous phase content i.e., RI fly ash. Furthermore, after firing to 1,000 °C, the density of samples prepared using fly ash RI remained approximately the same, while the compressive strength increased on average by 50%. In the other two types of fly ash the density increased slightly after firing, due to significant shrinkage, and compressive strength increased by as much as 800%. X-ray powder diffraction analysis confirmed the occurrence of a crystallization process after firing to 1,000 ° C, which resulted in newly formed crystal phases, including nepheline, sodalite, tridymite, and gehlenite.
Keywords: foamed alkali activated materials, geopolymers, properties, micro-CT
Published in DiRROS: 22.08.2023; Views: 225; Downloads: 146
.pdf Full text (7,94 MB)
This document has many files! More...

2.
Biophysical properties of foamed and solid polymers used in orthotics and prosthetics
Klemen Bohinc, Anže Abram, Anamarija Zore, Roman Štukelj, Ana Lenarčič, Rajko Vidrih, Andrijana Sever Škapin, 2021, original scientific article

Abstract: Orthotic and prosthetic materials should have good mechanical and antibacterial properties. Therefore, in our study, we consider four common foamed closed-cells and two solid polymeric materials regarding their mechanical behaviour and tendency for bacterial adhesion. For all materials, the surface roughness, hydrophobicity, zeta potential, tensile properties, hardness and CIE color parameters were measured. We found that foamed polymeric materials have higher roughness, higher hydrophobicity, lower Young's modulus, lower maximum tensile strength and lower hardness than solid materials. Bacterial adhesion test measurements based on observation by scanning electron microscopy show much a lower adhesion extent of S. aureus on solid materials than on foamed materials. The measured biophysical properties could be the key data for users to select the optimal materials.
Keywords: surface characterization, bacterial adhesion, foamed materials, prosthetic and orthotic material, surfaces
Published in DiRROS: 22.05.2023; Views: 242; Downloads: 157