20.500.12556/DiRROS-17258 Flame spread behaviour of Polydimethylsiloxane (PDMS) membranes in 1 g and µg environments Diffusion flame behaviour and silica ash (SiO2) production were experimentally studied for various Polydimethylsiloxane (PDMS) membrane thicknesses (0.125 mm to 1.0 mm) in normal gravity and during microgravity flight experiments. The flames were established on vertical samples (300 mm in length) and subjected to either opposed or concurrent forced flows (both laminar and turbulent), assimilating the NASA Test 1 that is in use for spacecraft material selection. The opposed flame spread rate was observed to be steady and could be estimated using classical theory. Under concurrent flow, the flame spread rate was only steady for very high forced flows. The opposed flame-spread rate ranged from 0.5 to 1.5 mm/s, while the concurrent case ranged between 0.1 and 12 mm/s. The transport of silica ash (SiO2) was found to affect the heat balance of the concurrent flame spread in a manner that resulted in unsteady flame spread. For opposed flame spread, on the other hand, the transport of silica ash showed to be irrelevant. The extinction behaviour for the concurrent flame spread was heavily dominated by the transport of silica-ash, while for opposed flames, extinction was due to kinetics (at high forced flows). In microgravity environments, the transport and deposition of silica ash is anticipated to dominate flame spread and near-limit as well. These results suggest that silica-based products might be less flammable in microgravity than other similar materials such as common thermoplastics (PP or PE) used as wire jackets. silicone burning spacecraft fire safety flame spread near-limit silica-ash požarno inženirstvo true false true Elsevier Science Angleški jezik Slovenski jezik © 2022 The Combustion Institute. Published by Elsevier Inc. All rights reserved. Neznano 2023-11-13 08:46:12 2023-11-13 08:55:50 2023-11-14 03:37:35 0000-00-00 00:00:00 2022 0 0 Opis vira z dne 1. 3. 2023; Nasl. z nasl. zaslona; 0000-00-00 PostprintKoncna Objavljeno NiDoloceno 0000-00-00 0000-00-00 2022-02-05 2024-02-05 620.1/.2 1556-2921 10.1016/j.combustflame.2022.112009 97359363 https://www.sciencedirect.com/science/article/abs/pii/S0010218022000281?via%3Dihub 1 55b2b4de-81f0-11ee-9ccb-001a4af901a5 https://dirros.openscience.si/Dokument.php?lang=slv&id=23431 RAZ_Rojas_Alva_Wilson_Ulises_2022.pdf RAZ_Rojas_Alva_Wilson_Ulises_2022.pdf 1 8DCDDE27E19B32DF34D5A296F581A9D7 d2f45b4e6a34c82f1a9d75386eb9ee65a3770a83816860584f3db5d331aac9cc 6c73ba50-81f1-11ee-9ccb-001a4af901a5 https://dirros.openscience.si/Dokument.php?lang=slv&id=23433 Zavod za gradbeništvo Slovenije 0 0 0