Development of multi-component fluoropolymer based coating on simulated outdoor patina on quaternary bronze
Tadeja Kosec, Luka Škrlep, Erika Švara Fabjan, Andrijana Sever Škapin, Giulia Masi, Elena Bernardi, Cristina Chiavari, Claudie Josse, Jerome Esvan, Luc Robbiola, 2019, izvirni znanstveni članek

Povzetek: Bronze reacts with oxygen, humidity, and pollutants in the atmosphere so that a patina forms. Natural exposure to an outdoor atmosphere can be simulated and accelerated in order to achieve a patina that mimics outdoor ancient patina. In order to avoid the uncontrolled dissolving of either the natural or artificially formed patina, protection of the patina is needed. In this study, a multi-component fluoropolymer based coating for the protection of bronze patina was developed. In order to provide various functionalities of the coating (such as the hydrophobicity of the coating surface, obtaining interactions within the coating itself as well as a bronze substrate and inhibiting the corrosion processes), a fluoroacrylate coating with appropriate adhesion promoter was suggested, with and without a silane modified benzotriazole inhibitor. The protective efficiency and durability of the applied coatings were investigated electrochemically using potentiodynamic tests and electrochemical impedance spectroscopy in a simulated acid rain solution. All of the developed coatings showed a significant decrease in the corrosion current density. The self-assembled single layer coating (FA-MS) also showed 100% inhibition efficiency. After ageing the coating remained transparent and did not change by UV exposure and/or thermal cycling. The patina and coating investigations using FIB-SEM and EDX showed that the latter coating (FA-MS) successfully covered the surface of the patinated bronze. The mechanism of the bonding was proposed and supported with the spectroscopic observation of a thin and even coating.
Ključne besede: bronze, patina, fluoropolymer coating, atmospheric corrosion
Objavljeno v DiRROS: 25.10.2023; Ogledov: 318; Prenosov: 170
.pdf Celotno besedilo (2,17 MB)
Gradivo ima več datotek! Več...

2.
Exploring the protection mechanism of a combined fluoropolymer coating on sulphide patinated bronze
Tadeja Kosec, Živa Novak, Erika Švara Fabjan, Luka Škrlep, Matjaž Finšgar, 2022, izvirni znanstveni članek

Povzetek: When bronze or artificially patinated bronze is exposed to an outdoor environment that contains aggressive ions such as sulphates, nitrates, and carbonates, the surface of the bronze changes its appearance due to the formation of corrosion products on the surface. Research is being conducted on versatile protective measures that can be used to protect the surface from these changes. A recently synthesised fluoropolymer-based coating with mercaptopropyl groups, i.e. a 3-component fluoropolymer coating FA-MS-SH (silane-modified poly methylmethacrylate (MS) with added mercaptopropyltrimethoxy silane (SH) and a fluoroacrylate (FA)) was explored in detail in this work where its protective mechanism on sulphide patinated bronze was investigated. Electrochemical tests were conducted on the sulphide patinated bronze with and without the 3-component coating FA-MS-SH. Furthermore, FA, MS and SH alone and various combinations and concentrations of FA-MS were studied in order to determine the protective effect and properties of each component. Colour change and contact angle measurements were also defined. FIB-SEM measurements and GCIB-XPS depth profiles were carried out to study surface bonding with the sulphide patina in detail. A mechanism for the protection of sulphide patinated bronze was presented through the use of a multianalytical tool approach. It was shown that FA physisorbed on the patinated surface, while MS and blends of the components chemisorbed on the layer of sulphide patinated bronze, also resulting in the surface being efficiently protected from corrosion processes.
Ključne besede: bronze, protection, brown patina, fluoropolymer coating
Objavljeno v DiRROS: 31.05.2023; Ogledov: 301; Prenosov: 174
.pdf Celotno besedilo (7,67 MB)
Gradivo ima več datotek! Več...

3.
Properties of the fluoroacrylate and methacryloxypropyl-trimethoxysilane applied to a layer of Cu2O on bronze as either single or multi-component coatings
Luka Škrlep, Tadeja Kosec, Matjaž Finšgar, Andrijana Sever Škapin, Erika Švara Fabjan, 2023, izvirni znanstveni članek

Povzetek: Various coatings have been developed and explored to protect bronze surfaces against the uncontrolled formation of different corrosion products when exposed to outdoor environments. In this research, the surfaces of artificially-formed oxidized bronze patinas (OB), consisting of Cu2O, were covered with either a single-component (fluoroacrylate, FA or methacryloxypropyl-trimethoxysilane, MS) or multi-component (a mixture of FA and MS, FA-MS) fluoropolymer coating and investigated. Variations in the concentration of each component in the coating were studied. Electrochemical tests were performed to determine the corrosion protection efficiency, followed by detailed surface analyses of the OBs, both uncoated and covered with single and multi-component coatings. A variety of investigative methods were used, including focused ion beam scanning electron microscopy (FIB-SEM), X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and time-of-flight secondary ion mass spectrometry (ToF-SIMS). The coating made from a combination of FA and MS resulted in a very high protection efficiency. Despite the increased hydrophilicity of the single MS component, however, it was shown to efficiently protect the oxidized bronze surface. The FA-MS systems showed high hydrophobicity, but no improvement was measured in the efficiency of the corrosion protection when it was compared to the coating that contained 10% MS. According to XPS and ToF-SIMS imaging, the FA component of the FA-MS coating was not present only on the uppermost surface of the coating but throughout the whole coating, which could affect its corrosion protection efficiency.
Ključne besede: bronze, Cu2O layer on bronze, fluoropolymer coating, protection efficiency, surface spectroscopy